Eurostar Staramide RF004EU PA66/6, 20% Glass Fiber Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 20% Glass Fiber Reinforced |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide RF004EU PA66/6, 20% Glass Fiber Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide RF004EU is a 20% Glass Fiber Reinforced Polyamide 66/6 Injection Molding (also known as Staramide 66C 20V S4)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm @Thickness 4.00 mm |
0.0010 - 0.0040 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 |
| Elongation at Break | >= 3.0 % | >= 3.0 % | ISO 527 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 195 MPa | 28300 psi | ISO 178 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80x10x4; ISO 179/1eA |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | 80x10x4; ISO 180/1U |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eU |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C @Thickness 3.20 mm |
430 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 255 - 275 °C | 491 - 527 °F | |
| Zone 2 | 265 - 275 °C | 509 - 527 °F | |
| Zone 3 | 265 - 275 °C | 509 - 527 °F | |
| Melt Temperature | 265 - 275 °C | 509 - 527 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® XCY630 PC+ABS (Europe-Africa-Middle East)
- Michelman® Micryl™ 766R Water resistant coating
- Kuraray HYBRAR® HD2 Thermoplastic Rubber-HDPE Blend
- Sylvin Technologies 9960-65 Natural PVC Molding Compound
- SABIC Innovative Plastics Valox® 855 PBT (Europe-Africa-Middle East)
- Dow Corning SILASTIC® LS 4-9080 FLUOROSILICONE RUBBER
- Fainplast Compounds FR 0117 Flexible PVC, Insulation
- Arkema Group KYNAR® 2821-00 Polyvinylidene Fluoride Powder
- DuPont Performance Polymers Hypalon® 40S Chlorosulfonated Polyethylene Rubber, General Description (discontin
- Quantum PEI - Ultem® 30% Glass Fiber Filled
Copyright © lookpolymers.com All Rights Reserved