DuPont Performance Polymers Zytel® LM70G35HSLX BK314 Nylon 66 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® LM70G35HSLX BK314 Nylon 66
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® LM70G35HSLX is a 35% glass fiber reinforced, heat stabilized, lubricated polyamide 66 for injection molding. It is well suited for laser marking.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | DAM; ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm |
0.0030 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 2.00 mm |
0.011 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 210 MPa @Temperature 23.0 °C |
30500 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | 2.9 % @Temperature 23.0 °C |
2.9 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 4.9 % @Temperature 23.0 °C |
4.9 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 8.50 GPa @Temperature 23.0 °C |
1230 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 11.0 GPa @Temperature 23.0 °C |
1600 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A |
| 17.0 kJ/m² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 180/1A | |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eU |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| 1.70 J/cm² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | DAM; ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm @Temperature 23.0 °C |
1.00e+11 ohm-cm @Temperature 73.4 °F |
50%RH; IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 295 °C | 563 °F | DAM; Optimum |
| 285 - 305 °C | 545 - 581 °F | DAM | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM |
| 100 °C | 212 °F | DAM; optimum | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Forms | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Material Status | Preliminary Data | DAM |
| Part Marking Code | >PA66-GF35< | ISO 11469; DAM |
| Processing Method | injection Molding | DAM |
| Product Category | Glass Reinforced Resins | DAM |
| Resin Identification | PA66-GF35 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |