- Polymer Property : Tensile Strength at Break = 21800 psi
Polymer Property : Tensile Strength at Break = 21800 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 150 MPa @Temperature 250 °C |
>= 21800 psi @Temperature 482 °F |
|
| PEAK Werkstoff DISPAL S250 Aluminum Alloy, AlSi20Fe5Ni2, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
ISO 527 |
| Victrex® PEEK 450FC30 General Purpose Product Description: High performance thermoplastic material, 30% reinforced with carbon fibre / graphite / PTFE PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and ext.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 125 °C |
21800 psi @Temperature 257 °F |
ISO 527 |
| Victrex® PEEK 650CA30 30% Carbon Fiber Filled, PolyEtherEtherKetone High performance thermoplastic material, 30% carbon fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and extrusion, low flow, FDA food contact compliant.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 125 °C |
21800 psi @Temperature 257 °F |
ISO 527 |
| Victrex® PEEK 90GL60 Polyetheretherketone, 60% Glass Fibre Reinforced Product Description:High performance thermoplastic material, 60% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, standard flow, FDA food contac.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| DuPont Performance Polymers Zytel® LM70G35HSLX BK314 Nylon 66
(Unverified Data**) Zytel® LM70G35HSLX is a 35% glass fiber reinforced, heat stabilized, lubricated polyamide 66 for injection molding. It is well suited for laser marking.Information provided by DuPont Performance Po.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 120 °C |
21800 psi @Temperature 248 °F |
|
| LATI Laramid G/45 PPA, 45% Glass Fiber Reinforced Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; .. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 150 °C |
21800 psi @Temperature 302 °F |
|
| LATI Larpeek 10 G/50 PEEK, 50% Glass Fiber Reinforced Polyetheretherketone (PEEK) based compound. Glass fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
|
| LATI Larton K/20 PPS, 20% Carbon Fiber Reinforced Polyphenylene Sulfide (PPS) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
|
| LATI Latamid 12 G/50 PA 12, 50% Glass Fiber Reinforced Polyamide 12 (PA12) based compound. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
|
| LATI Latamid 6 H2E04 G/30 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Toughened. Glass fibers. Good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 60.0 °C |
21800 psi @Temperature 140 °F |
|
| LATI Latamid 66 H2 G/50-GWHF1 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. improved G.W.F.I. compared to standard product.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North Ameri.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
|
| LATI Latamid 66 VH2 G/30 PA 66, 30% Glass Fiber Reinforced Polyamide 66 (PA66) based compound. Improved thermal stabilization. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati In.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 60.0 °C |
21800 psi @Temperature 140 °F |
|
| LATI Laramid G/30 PPA, 30% Glass Fiber Reinforced Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; .. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 120 °C |
21800 psi @Temperature 248 °F |
|
| LATI Larpeek 10 G/40 PEEK, 40% Glass Fiber Reinforced Polyetheretherketone (PEEK) based compound. Glass fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 90.0 °C |
21800 psi @Temperature 194 °F |
|
| LATI Larton G/40 I6 PPS, 40% Glass Fiber Reinforced Polyphenylene Sulfide (PPS) based compound. Glass fibers. Good elongation. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa .. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
|
| LATI Latamid 66 H2 G/25-V0HF1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Very good mechanical properties. Very good electrica.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
|
| LATI Later 4 K/30 PBT, 30% Carbon Fiber Reinforced Polybutylene Terephthalate (PBT) based compound. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplasti.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
DAM; ISO 527 |
| DuPont Performance Polymers Zytel® 84G33 BKB031 Nylon 66
(Unverified Data**) Zytel® 84G33 BKB031 is a 33% glass reinforced toughened polyamide 66 and polyamide 6 co-melt black cube blended resin. This resin was developed for applications requiring strength, stiffness and im.. |
|||
| Tensile Strength at Break | 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| DuPont Performance Polymers Zytel® 70G35HSRX BK099 Nylon 66
(Unverified Data**) Zytel® 70G35HSRX BK099 a 35% glass reinforced, heat stabilized, hydrolysis resistant PA66 for injection molding. Developed for applications designed for direct overmolding of gaskets onto thermopla.. |
|||