DuPont Performance Polymers Zytel® 73G30HSL NC010 Nylon 6 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® 73G30HSL NC010 Nylon 6
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® 73G30HSL NC010 is a 30% glass fiber reinforced, heat stabilized polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | DAM; ISO 1183 |
| Filler Content | 30 % | 30 % | DAM |
| Water Absorption | 1.9 % @Temperature 23.0 °C |
1.9 % @Temperature 73.4 °F |
Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 6.3 % @Temperature 23.0 °C |
6.3 % @Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm |
0.0020 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 2.00 mm |
0.0060 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Melt Index of Compound | 4.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
DAM; cm3/10 min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa @Temperature 23.0 °C |
16700 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 185 MPa @Temperature 23.0 °C |
26800 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | 3.5 % @Temperature 23.0 °C |
3.5 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 6.0 % @Temperature 23.0 °C |
6.0 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 5.80 GPa @Temperature 23.0 °C |
841 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 9.70 GPa @Temperature 23.0 °C |
1410 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 180/1A |
| 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 180/1A | |
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A | |
| 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 180/1A | |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eU |
| 8.40 J/cm² @Temperature -30.0 °C |
40.0 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eU | |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eU | |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA |
| 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA | |
| 2.10 J/cm² @Temperature -30.0 °C |
9.99 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |
| 2.30 J/cm² @Temperature 23.0 °C |
10.9 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eA | |
| Tensile Creep Modulus, 1 hour | 6190 MPa @Temperature 23.0 °C |
898000 psi @Temperature 73.4 °F |
50%RH; ISO 899 |
| Tensile Creep Modulus, 1000 hours | 4630 MPa @Temperature 23.0 °C |
672000 psi @Temperature 73.4 °F |
50%RH; ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 102 µm/m-°C @Temperature 23.0 - 55.0 °C |
56.7 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 |
| 102 µm/m-°C @Temperature 23.0 - 55.0 °C |
56.7 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| Melting Point | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | DAM; ISO 75-1/-2 |
| Glass Transition Temp, Tg | 65.0 °C | 149 °F | 10°C/min; DAM; ISO 11357-1/-2 |
| UL RTI, Electrical | 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
DAM; UL 746B |
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
DAM; UL 746B |
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
DAM; UL 746B | |
| 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0591 in |
DAM; UL 746B |
| 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
DAM; UL 746B | |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; IEC 60695-11-10 |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
DAM; UL94 | |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; UL94 | |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; UL94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 °C | 518 °F | DAM; Optimum |
| 260 - 280 °C | 500 - 536 °F | DAM | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM |
| 100 °C | 212 °F | DAM; optimum | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | DAM |
| Lubricant | DAM | |
| Appearance | Natural Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Features | Chemical Resistance, Good | DAM |
| Fatigue Resistant | DAM | |
| Fuel Resistant | DAM | |
| Grease Resistant | DAM | |
| Heat Aging Resistance, Good | DAM | |
| Heat Stabilized | DAM | |
| Oil Resistant | DAM | |
| Thermal Aging Resistance, Good | DAM | |
| Filler | Glass fiber reinforcement | DAM |
| Forms | Pellets | DAM |
| Generic | Nylon 6 | DAM |
| Material Status | Current | DAM |
| Part Marking Code | >PA6-GF30< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA6 | DAM |
| Processing Method | Injection Molding | DAM |
| Product Category | Glass Reinforced Resins | DAM |
| Region Available - Global | Yes | DAM |
| Resin Identification | PA6-GF30 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
| Uses | Appliance Components | DAM |
| Automotive Applications | DAM | |
| Electrical/Electronic Applications | DAM | |
| High Gloss Applications | DAM | |
| Industrial Applications | DAM |
Users viewing this material also viewed the following:
- Oceanchem Group Triethyl Phosphate (TEP)
- Pyrotek TS-125 Thermoset Electrical Insulation Product
- MetalTek HAYNES® 230 Severe Corrosion and Heat Resistant Alloy
- Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry)
- Solvay Specialty Polymers FOMBLIN® Y L-VAC 06/6 PFPE Pump Oil
- Saint-Gobain CHR® SG33-10(R) Industrial Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- Formosa Plastics Formolon® 38 PVC
Copyright © lookpolymers.com All Rights Reserved