DuPont Performance Polymers Hytrel® G4078W TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® G4078W TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hytrel® G4078W is a low modulus grade with nominal hardness of 40D. It contains non-discoloring stabilizer. It can be processed by many conventional thermoplastic processing techniques like injection molding and extrusion.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Water Absorption 0.40 %

@Temperature 23.0 °C
 0.40 %

@Temperature 73.4 °F
 Equilibrium 50%RH; ISO 62
2.1 %

@Temperature 23.0 °C
 2.1 %

@Temperature 73.4 °F
 Immersion 24h; ISO 62
3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
 Immersion 24h; ASTM D570
3.7 %

@Temperature 23.0 °C
 3.7 %

@Temperature 73.4 °F
 Saturation, immersed; ISO 62
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
Flow; ASTM D955
Linear Mold Shrinkage, Flow 0.0080 cm/cm

@Thickness 2.00 mm
 0.0080 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm

@Thickness 2.00 mm
 0.0080 in/in

@Thickness 0.0787 in
 ISO 294-4
Melt Flow 5.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 5.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ASTM D1238
5.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 5.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Melt Index of Compound 5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D <= 40
<= 40
ASTM D2240
<= 40
<= 40
ISO 868
35

@Time 15.0 sec
 35

@Time 0.00417 hour
 ISO 868
Tensile Strength at Break 17.0 MPa

@Temperature 23.0 °C
 2470 psi

@Temperature 73.4 °F
 ISO 527 (1BA bar)
17.0 MPa

@Temperature 23.0 °C
 2470 psi

@Temperature 73.4 °F
 ASTM D638
Tensile Stress 0.900 MPa

@Strain 3.65 %,
Temperature 120 °C
 131 psi

@Strain 3.65 %,
Temperature 248 °F
 ISO 527
1.10 MPa

@Strain 3.28 %,
Temperature 100 °C
 160 psi

@Strain 3.28 %,
Temperature 212 °F
 ISO 527
1.11 MPa

@Strain 3.21 %,
Temperature 90.0 °C
 161 psi

@Strain 3.21 %,
Temperature 194 °F
 ISO 527
1.33 MPa

@Strain 3.19 %,
Temperature 60.0 °C
 193 psi

@Strain 3.19 %,
Temperature 140 °F
 ISO 527
1.34 MPa

@Strain 6.97 %,
Temperature 120 °C
 194 psi

@Strain 6.97 %,
Temperature 248 °F
 ISO 527
1.61 MPa

@Strain 9.62 %,
Temperature 120 °C
 234 psi

@Strain 9.62 %,
Temperature 248 °F
 ISO 527
1.64 MPa

@Strain 3.22 %,
Temperature 40.0 °C
 238 psi

@Strain 3.22 %,
Temperature 104 °F
 ISO 527
1.69 MPa

@Strain 6.20 %,
Temperature 100 °C
 245 psi

@Strain 6.20 %,
Temperature 212 °F
 ISO 527
1.71 MPa

@Strain 6.06 %,
Temperature 90.0 °C
 248 psi

@Strain 6.06 %,
Temperature 194 °F
 ISO 527
1.89 MPa

@Strain 12.94 %,
Temperature 120 °C
 274 psi

@Strain 12.94 %,
Temperature 248 °F
 ISO 527
2.11 MPa

@Strain 16.26 %,
Temperature 120 °C
 306 psi

@Strain 16.26 %,
Temperature 248 °F
 ISO 527
2.11 MPa

@Strain 3.37 %,
Temperature 23.0 °C
 306 psi

@Strain 3.37 %,
Temperature 73.4 °F
 ISO 527
2.12 MPa

@Strain 6.03 %,
Temperature 60.0 °C
 307 psi

@Strain 6.03 %,
Temperature 140 °F
 ISO 527
2.15 MPa

@Strain 9.12 %,
Temperature 100 °C
 312 psi

@Strain 9.12 %,
Temperature 212 °F
 ISO 527
2.20 MPa

@Strain 8.92 %,
Temperature 90.0 °C
 319 psi

@Strain 8.92 %,
Temperature 194 °F
 ISO 527
2.29 MPa

@Strain 19.58 %,
Temperature 120 °C
 332 psi

@Strain 19.58 %,
Temperature 248 °F
 ISO 527
2.34 MPa

@Strain 3.31 %,
Temperature 0.000 °C
 339 psi

@Strain 3.31 %,
Temperature 32.0 °F
 ISO 527
2.44 MPa

@Strain 22.9 %,
Temperature 120 °C
 354 psi

@Strain 22.9 %,
Temperature 248 °F
 ISO 527
2.44 MPa

@Strain 11.31 %,
Temperature 100 °C
 354 psi

@Strain 11.31 %,
Temperature 212 °F
 ISO 527
2.50 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 363 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ISO 527 (1BA bar)
2.56 MPa

@Strain 26.22 %,
Temperature 120 °C
 371 psi

@Strain 26.22 %,
Temperature 248 °F
 ISO 527
2.59 MPa

@Strain 8.16 %,
Temperature 60.0 °C
 376 psi

@Strain 8.16 %,
Temperature 140 °F
 ISO 527
2.60 MPa

@Strain 11.77 %,
Temperature 90.0 °C
 377 psi

@Strain 11.77 %,
Temperature 194 °F
 ISO 527
2.65 MPa

@Strain 28.87 %,
Temperature 120 °C
 384 psi

@Strain 28.87 %,
Temperature 248 °F
 ISO 527
2.69 MPa

@Strain 6.08 %,
Temperature 40.0 °C
 390 psi

@Strain 6.08 %,
Temperature 104 °F
 ISO 527
2.74 MPa

@Strain 32.19 %,
Temperature 120 °C
 397 psi

@Strain 32.19 %,
Temperature 248 °F
 ISO 527
2.75 MPa

@Strain 14.23 %,
Temperature 100 °C
 399 psi

@Strain 14.23 %,
Temperature 212 °F
 ISO 527
2.81 MPa

@Strain 35.51 %,
Temperature 120 °C
 408 psi

@Strain 35.51 %,
Temperature 248 °F
 ISO 527
2.90 MPa

@Strain 38.83 %,
Temperature 120 °C
 421 psi

@Strain 38.83 %,
Temperature 248 °F
 ISO 527
2.90 MPa

@Strain 14.63 %,
Temperature 90.0 °C
 421 psi

@Strain 14.63 %,
Temperature 194 °F
 ISO 527
2.97 MPa

@Strain 42.15 %,
Temperature 120 °C
 431 psi

@Strain 42.15 %,
Temperature 248 °F
 ISO 527
3.00 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 435 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ASTM D638
3.01 MPa

@Strain 44.8 %,
Temperature 120 °C
 437 psi

@Strain 44.8 %,
Temperature 248 °F
 ISO 527
3.02 MPa

@Strain 17.15 %,
Temperature 100 °C
 438 psi

@Strain 17.15 %,
Temperature 212 °F
 ISO 527
3.07 MPa

@Strain 48.12 %,
Temperature 120 °C
 445 psi

@Strain 48.12 %,
Temperature 248 °F
 ISO 527
3.11 MPa

@Strain 11.0 %,
Temperature 60.0 °C
 451 psi

@Strain 11.0 %,
Temperature 140 °F
 ISO 527
3.13 MPa

@Strain 51.44 %,
Temperature 120 °C
 454 psi

@Strain 51.44 %,
Temperature 248 °F
 ISO 527
3.16 MPa

@Strain 17.48 %,
Temperature 90.0 °C
 458 psi

@Strain 17.48 %,
Temperature 194 °F
 ISO 527
3.17 MPa

@Strain 54.76 %,
Temperature 120 °C
 460 psi

@Strain 54.76 %,
Temperature 248 °F
 ISO 527
3.22 MPa

@Strain 58.08 %,
Temperature 120 °C
 467 psi

@Strain 58.08 %,
Temperature 248 °F
 ISO 527
3.24 MPa

@Strain 20.06 %,
Temperature 100 °C
 470 psi

@Strain 20.06 %,
Temperature 212 °F
 ISO 527
3.26 MPa

@Strain 5.83 %,
Temperature 23.0 °C
 473 psi

@Strain 5.83 %,
Temperature 73.4 °F
 ISO 527
3.27 MPa

@Strain 61.4 %,
Temperature 120 °C
 474 psi

@Strain 61.4 %,
Temperature 248 °F
 ISO 527
3.30 MPa

@Strain 64.05 %,
Temperature 120 °C
 479 psi

@Strain 64.05 %,
Temperature 248 °F
 ISO 527
3.33 MPa

@Strain 67.37 %,
Temperature 120 °C
 483 psi

@Strain 67.37 %,
Temperature 248 °F
 ISO 527
3.34 MPa

@Strain 19.62 %,
Temperature 90.0 °C
 484 psi

@Strain 19.62 %,
Temperature 194 °F
 ISO 527
3.37 MPa

@Strain 70.69 %,
Temperature 120 °C
 489 psi

@Strain 70.69 %,
Temperature 248 °F
 ISO 527
3.40 MPa

@Strain 74.01 %,
Temperature 120 °C
 493 psi

@Strain 74.01 %,
Temperature 248 °F
 ISO 527
3.43 MPa

@Strain 22.98 %,
Temperature 100 °C
 497 psi

@Strain 22.98 %,
Temperature 212 °F
 ISO 527
3.44 MPa

@Strain 77.33 %,
Temperature 120 °C
 499 psi

@Strain 77.33 %,
Temperature 248 °F
 ISO 527