Polymer Property : Tensile Stress = 2.59 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Stress 2.59 MPa

@Strain 300 %
376 psi

@Strain 300 %
ASTM D412
Polymax® Maxelast® A9855A TPE, ABS/PC Overmold
Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesAuto PartsTool Hand GripsSporting GoodsWire & Cable ElectronicsMedical DevicesInform..
Tensile Stress 2.59 MPa

@Strain 25.0 %
375 psi

@Strain 25.0 %
Average; ASTM D412 Method A
Seals Eastern 7352D Nano-PTFE Filled Fluoroelastomer
Nano-PTFE filled fluoroelastomer for low wear in hot dynamic applicationsInformation provided by Seals Eastern.
Tensile Stress 2.59 MPa

@Strain 5.25 %,
Temperature -20.0 °C
376 psi

@Strain 5.25 %,
Temperature -4.00 °F
TPE; ISO 11403-1 -2
DuPont Performance Polymers Hytrel® 3078 Polyester Elastomer TPC-ET  (Unverified Data**)
30 Shore D High Performance Polyester Elastomer with Non-discoloring Stabilizer Hytrel 3078 is a very low modulus grade with nominal hardness of 30D. It contains non-discoloring stabilizer. It can b..
Tensile Stress 2.59 MPa

@Strain 5.25 %,
Temperature -20.0 °C
376 psi

@Strain 5.25 %,
Temperature -4.00 °F
TPE; ISO 11403-1 -2
DuPont Performance Polymers Hytrel® 3078FG Polyester Elastomer TPC-ET  (Unverified Data**)
30 Shore D High Performance Polyester Elastomer Developed for Food Contact ApplicationsInformation provided by DuPont Performance Polymers
Tensile Stress 2.59 MPa

@Strain 8.16 %,
Temperature 60.0 °C
376 psi

@Strain 8.16 %,
Temperature 140 °F
ISO 527
DuPont Performance Polymers Hytrel® G4078W TPC-ET  (Unverified Data**)
Hytrel® G4078W is a low modulus grade with nominal hardness of 40D. It contains non-discoloring stabilizer. It can be processed by many conventional thermoplastic processing techniques like inject..