- DSM EcoPaXX® Q-X07290 PA410-I
DSM EcoPaXX® Q-X07290 PA410-I
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | EcoPaXX® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM EcoPaXX® Q-X07290 PA410-I.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact Modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.80 % | 1.80 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | cond; ISO 527-1/-2 |
| 65.0 MPa | 9430 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 45 % | 45 % | dry; ISO 527-1/-2 |
| >= 50 % | >= 50 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 1.30 GPa | 189 ksi | cond; ISO 527-1/-2 |
| 2.50 GPa | 363 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 50.0 MPa | 7250 psi | cond; ISO 178 |
| 95.0 MPa | 13800 psi | dry; ISO 178 | |
| Flexural Modulus | 1.30 GPa | 189 ksi | cond; ISO 178 |
| 2.40 GPa | 348 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | dry; ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | cond; IEC 60093 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | cond; IEC 60243-1 |
| 34.0 kV/mm | 864 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | cond; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Calculated Bio Based Carbon Content (%) | 66 | ASTM 6866 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C6600 PC+ABS (Asia Pacific)
- NCMT NanoPAC™ HG602 High Performance Polypropylene Nanocomposite
- MarkeTech Silicon Single Crystal Semiconductor Wafer, p-type, Boron Doped, Czochralski-LED Grown
- Heraeus Cleviosâ„¢ PH Conductive Sulfonate Polymer for Antistatic Coatings
- A. Schulman LP552-01 Injection Molding, Extrusion Grade Compound
- Trelleborg R480 Commercial Natural Rubber Polyisoprene
- Dow Corning HV 490 EMULSION
- Eurotec® Tecomid® NB40 GR15 NL XA70 PA6, 15% glass fiber reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural
- AlphaGary Evoprene™ GC 5617 SEBS Thermoplastic Elastomer
- Beijing Ranger Chem BLUESTAR® 1079 PBT
Copyright © lookpolymers.com All Rights Reserved