Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
Polycasa XT 630 PMMA QUINN XT sheets have good optical properties and a brilliant surface. QUINN XT sheets offer excellent transparency, good mechanical properties, are UV resistant, have very good weathering and ageing.. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 915AU PC (Asia Pacific) LEXAN resin grade 915AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in transparent colors, inte.. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® 915AU PC (Europe-Africa-Middle East) LEXAN resin grade 915AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in transparent colors, inte.. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 923X PC (Asia Pacific) Lexan*923x is a UV stabilized high flow impact modified injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, low temperatur.. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
Radici Radilon® S 35FL (dry) Nylon 6 Radilon® S (homopolyamides) are normally used in cast and blown extrusion for the production of packaging films. Radilon® S grades can be extruded to a thickness varying from 20 mm to 100 mm.Appl.. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® LUX9136C PC COPOLYMER Lexan* LUX9136C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and.. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® OQ1022 PC Standard Flow OQ Resin |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® SLX2531T PC Copolymer (Asia Pacific) Transparent weatherable PC copolymer for blowmolding/extrusion. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® FXC810MA PC+ABS (Europe-Africa-Middle East) CYCOLOY FXC810MA is a multi-purpose PC+ABS injection moulding grade, suitable for those applications that require marble colour effects. The colour package may effect performance.This data was suppl.. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® CFR5630D PC COPOLYMER (Europe-Africa-Middle East) LEXAN™ CFR5630D Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC resin meets FAR25.853 smoke density a.. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® CFR9131 PC COPOLYMER (Europe-Africa-Middle East) Lexan* CFR9131 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and .. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
Nilit FRIANYL B63 ND Nylon 6 Nylon 6, low viscosity, permanently flexible, dry impact resistant (dowels).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
LG Chemical Lupoy 1621-02 Polycarbonate Resin Description: LUPOY PC 1621-02 resin is designed for large injection stretch blow molding and extrusion blow molding parts. It exhibits an excellent physical property balance of heat resistance, tran.. |
|||
Flexural Modulus | 2.40 - 2.60 GPa | 348 - 377 ksi | ASTM D790 |
Loxim 830 02T HB Polypropylene Compound, 30% Talc Filled, Flame Retardant Information provided by Loxim Industries |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
Mitsubishi Xantar® 24 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
Mitsubishi Xantar® F 22 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP IN001 PA6.12 LNP* LUBRICOMP* IN001 is a compound based on Nylon 6/12 resin containing 2% Moly. Added feature of this grade is: Wear Resistant. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem ATX100R PEI (Europe-Africa-Middle East) Higher impact, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 HB Listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem HATX100 PEI+PCE Higher impact, high flow Polyetherimide blend. ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food.. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem HATX100 PEI+PCE (Europe-Africa-Middle East) Higher impact, high flow Polyetherimide blend. ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food.. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® IQ3001 PBT (Asia Pacific) Valox IQ3001 is an unfilled environmentally responsible iQ-PBT resin modified with elastomer. Targeted for flexible hinge applications. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
Spartech Royalite R60M Hi-Impact ABS/PVC Resin Data provided by the manufacturer. This rigid, fire-rated, proprietary resin is specifically formulated to meet the requirements of the FAR 25.853 A flammability test. Primary applications are air.. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 2.0 mm/min; ISO 178 |
Styron CALIBREâ„¢ 303-15 Polycarbonate Resin Overview: CALIBREâ„¢ 300-115 polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity. The CALIBREâ„¢ 300-10 series products are available in 4 .. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
Eastman Eastar MN058 Copolyester Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar MN058 Copolyester is a medical gra.. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
Covestro Makrolon® Rx2435 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices• Low.. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
Chi Mei Wonderlite® PC-115 Polycarbonate Low Viscosity |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
DuPont Performance Polymers Sorona® 3301V BK001 Polytrimethylene Terephthalate (PTT)
(Unverified Data**)& Unreinforced Renewably Sourced Polytrimethylene Terephthalate Sorona 3301V BK001 is an unreinforced black polytrimethylene terephthalate resin containing 35% renewably sourced ingredients by weight .. |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
Ashley Polymers Ashlene® P292 PPO Extrusion grade, highest heat deflection temperature and good impact strength.Data provided by the manufacturer |
|||
Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL PX2060 PPE+PS (Europe-Africa-Middle East) Noryl* PX2060 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR .. |