CeramTec 192/193 Titania

Category Ceramic , Oxide , Titanium Oxide
Manufacturer CeramTec North America
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CeramTec 192/193 Titania.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
192/193 is an excellent material for textile and other structural applications, where superior surface finishes are required with high chemical resistance. 193 is identical except it is metallic gray in color and conducts static electricity.
Physical Properties Metric English Comments
Density 4.00 g/cc
0.145 lb/in³
DIN EN 623-2 / ASTM-C373 / ASTM-C20
Water Absorption 0.00 %
0.00 %
DIN EN 623-2 / ASTM-C373
Mechanical Properties Metric English Comments
Vickers Microhardness 800
800
HV 0.5; DINV ENV 843-4
Tensile Strength at Break 51.6 MPa
7480 psi
ACMA Test #4 / DIN EN 843-1
Tensile Modulus 228 GPa
33100 ksi
Young's; DINV ENV 843-2 / ASTM-F417
Flexural Strength 137 MPa
19900 psi
20 x 40 mm
Compressive Strength 688 MPa
99800 psi
ASTM C-773-88 / DIN 51067T1
Poissons Ratio 0.27
0.27
DINV ENV 843-2
Fracture Toughness 3.20 MPa-m½
2.91 ksi-in½
DIN 51109
Shear Modulus 89.0 GPa
12900 ksi
Thermal Properties Metric English Comments
CTE, linear 8.80 µm/m-°C
4.89 µin/in-°F
DIN EN 821-1
8.30 µm/m-°C

@Temperature 20.0 - 200 °C
4.61 µin/in-°F

@Temperature 68.0 - 392 °F
9.00 µm/m-°C

@Temperature 20.0 - 600 °C
5.00 µin/in-°F

@Temperature 68.0 - 1110 °F
ASTM-C373
9.00 µm/m-°C

@Temperature 20.0 - 1000 °C
5.00 µin/in-°F

@Temperature 68.0 - 1830 °F
Specific Heat Capacity 0.700 J/g-°C

@Temperature 100 - 200 °C
0.167 BTU/lb-°F

@Temperature 212 - 392 °F
DINV ENV 821-3
Thermal Conductivity 11.9 W/m-K
82.6 BTU-in/hr-ft²-°F
DIN EN 821-2 / ASTM-C408
Maximum Service Temperature, Air 1000 °C
1830 °F
Electrical Properties Metric English Comments
Volume Resistivity 10000 ohm-cm

@Temperature 900 °C
10000 ohm-cm

@Temperature 1650 °F
1.70e+6 ohm-cm

@Temperature 500 °C
1.70e+6 ohm-cm

@Temperature 932 °F
9.80e+11 ohm-cm

@Temperature 100 °C
9.80e+11 ohm-cm

@Temperature 212 °F
IEC 672-1
>= 1.00e+12 ohm-cm

@Temperature 25.0 °C
>= 1.00e+12 ohm-cm

@Temperature 77.0 °F
ASTM-D257
Dielectric Constant 85

@Frequency 1.00e+6 Hz
85

@Frequency 1.00e+6 Hz
IEC 672-1 / ASTM-C150
Dielectric Strength 3.937 kV/mm
100.0 kV/in
6.35 mm (1/4") IEC 672-1
Dissipation Factor 0.00050

@Frequency 1.00e+6 Hz
0.00050

@Frequency 1.00e+6 Hz
0.0010

@Frequency 60.0 Hz
0.0010

@Frequency 60.0 Hz
0.0040

@Frequency 1.00e+10 Hz
0.0040

@Frequency 1.00e+10 Hz
Descriptive Properties Value Comments
Color Tan/Gray
Te Value (°C) 520
Thermal Shock Resistance R1 (K) 330
Hasselman (Experimental)