- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 150 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 150 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
| Multibase Multi-Pro® 1508 M Polypropylene Mica Filled, 15% by weight.Features:Rigidity, HighImpact Resistance, GoodForms:PelletsProcessing Methods:Injection MoldingUses:Automotive ApplicationsInformation provided by Multibase |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C @Thickness 3.18 mm |
150 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion 87736 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| RheTech Products HP519-01 26% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Black Applications: Interior trim moldingsSill platesAir ductsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| Nylene® 204 (HS) , Fast Cycle Nylon 6 Description: Nylene® 204 (HS) is a fast cycle, medium viscosity, nucleated nylon 6. 204 is UL approved and automotive approved. Information provided by Custom Resins.ALM, Nylene Canada, and Custom .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| Nylene® Vexel™ B12U FR Un-reinforced, Flame Retardant PBT Description: Vexel™ B12U FR is an un-reinforced, flame retardant PBT. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| Polymer Resources NY6-GP1-[color]-H General Purpose Nylon 6, Heat Stabilized General Purpose Nylon 6, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grade.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| Polymer Resources NY6-GP1-[color]H Nylon, General Purpose, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylon® N2000STHL Nylon 6 (DAM) Information provided by Ravago. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 - 82.0 °C | 150 - 180 °F | Average value: 74.8 °C Grade Count:34 |
| Overview of materials for PVC/Acrylic Alloy This property data is a summary of similar materials in the MatWeb database for the category "PVC/Acrylic Alloy". Each property range of values reported is minimum and maximum values of appropriate .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| Fiberfil® PP-61/TC/20 Polypropylene Copolymer, 20% Talc Information provided by FIBERFIL Engineered Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed (0.250"); ASTM D648 |
| LTL Color Compounds ColorFast® NYA1000 Nylon/ABS Alloy Nylon/ABS alloy with high ductility and excellent chemical resistanceAll information provided by LTL Color Compounders, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® HDPE TM30 30% Talc Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 30% Filler by WeightInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| Spartech PP5130 Talc Filled Homopolymer Offers an excellent balance of processing improvement and high levels of stiffness and heat deflection temperatureInformation provided by Spartech |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PA6/6,6 IM 5050 BK MB Nylon 6/66 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Copolymer, Impact Modified and LubricatedAppearance: BlackProcessing Metho.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM Test |
| Styrolution Terblend® N NM-19 ABS/PA6 (Dry) Terblend N NM-19 is a UV stabilized ABS/PA6 blend combining very high impact strength, even at low temperatures with an excellent processability and surface appearance.Information provided by STYROL.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PA6 E FR Availability: North AmericaForms: PelletsFeatures: Flame Retardant Processing Method: ExtrusionInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 MV5 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
| Chase Plastics CP Pryme® N300HL (Dry) Nylon 6, Heat Stabilized, Lubricated, Recycled Content Features: Heat StabilizedLubricatedRecycled contentForm: PelletsInformation provided by Chase Plastics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 MV5 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 MV5 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| Ecomass® 3620BX60 18% Borated Polyethylene (HDPE) 18% Borated Polyethylene (HDPE), Product Form - Pellets, No Pre-Drying RequiredProcessing Method: Injection Molding, Compression MoldingNeutron Shielding ApplicationsInformation provided by Technic.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
| Techmer ES Statiblend® PP TM10 BK Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 10% Filler by WeightFeatures: ConductiveUL File Number: E157318Appearance: BlackInformation provided by TP Composites, Inc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| Asahi Kasei Thermofil P-10CC-Y488 10% Calcium Carbonate Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 MV5 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D-648 |
| Axiall 3027 Rigid PVC, Extrusion Georgia Gulf 3027 is a powder blend designed as a substrate base for coextruded profiles.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||