BASF Ultramid® 8202 HS BK-102 PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8202 HS BK-102 PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8202 HS BK-102 is an unfilled, heat stabilized, pigmented black, low viscosity, general purpose injection molding PA6 exhibiting excellent fluidity for filling thin sections. It possesses the combination of strength, stiffness and toughness properties as well as excellent chemical, thermal and abrasion resistance. The heat stabilizer system extends its retention of properties at elevated temperatures.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 1.6 %
1.6 %
24 hour; ISO Test
9.5 %
9.5 %
ISO 62
Moisture Absorption at Equilibrium 2.7 %
2.7 %
23°C/50% R.H.; ISO 62
Relative Viscosity 2.6 cP
2.6 cP
ISO Test; 96 % SAV
Viscosity Measurement 48
48
Formic Acid
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ASTM Test
Tensile Strength, Yield 85.0 MPa
12300 psi
50mm/min; ISO 527
85.0 MPa
12300 psi
2 in/min; ASTM Test
Elongation at Break 25 %
25 %
50mm/min, Nominal strain; ISO 527
50 %
50 %
2 in/min; ASTM Test
Elongation at Yield 4.0 %
4.0 %
50mm/min; ISO 527
4.0 %
4.0 %
2 in/min; ASTM Test
Tensile Modulus 3.10 GPa
450 ksi
1mm/min; ISO 527
Flexural Strength 90.0 MPa
13100 psi
ISO Data
108 MPa
15700 psi
ASTM Test
Flexural Modulus 2.65 GPa
384 ksi
ISO Data
2.83 GPa
410 ksi
ASTM Test
Izod Impact, Notched 0.550 J/cm

@Thickness 3.17 mm
1.03 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Notched (ISO) 5.50 kJ/m²
2.62 ft-lb/in²
ISO Test
4.00 kJ/m²

@Temperature -40.0 °C
1.90 ft-lb/in²

@Temperature -40.0 °F
ISO Test
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 83.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
46.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 178 °C
352 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ISO 75
65.0 °C
149 °F
ASTM Test
Flammability, UL94 V-2

@Thickness 0.700 mm
V-2

@Thickness 0.0276 in
V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
Descriptive Properties Value Comments
Color BK-102
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes