Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
NatureWorks® Ingeo™ 3052D Lubricated, High Flow Biopolymer NatureWorks® PLA polymer 2003D is a thermoplastic resin derived from annually renewable resources. It is designed for injection molding applications where the requirements are clarity with heat def.. |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
NatureWorks® Ingeo™ 8052D Foam Grade Biopolymer Ingeo 8052D can be converted into an expanded foam sheet with use temperatures up to 77°F (25°C). This foam is lightweight, strong and suitable for packaging fresh meat and vegetables. In order to.. |
|||
Flexural Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 505R PC Lexan* 505R Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. Lexan 505R contains non-chlorinated, non-brominated flame retardant systems with UL-94 V0 rating at 1.5mm... |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
SABIC Innovative Plastics Lexan® JK2000 PC+ABS (Asia Pacific) Lexan* JK2000 compound is a glass reinforced, non-Br and non-Cl FR polycarbonate blends designed for thinwall molding applications. |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
Polymer Resources NY6-GP2-[color]-H General Purpose Nylon 6, Nucleated, Heat Stabilized General Purpose Nylon 6, Nucleated, Heat StabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades.. |
|||
Flexural Strength | 108 MPa | 15700 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL42 PC LNP* Lubricomp* DFL-4042 a compound based on Polycarbonate resin containing 10% Glass Fiber, 20% PTFE. Added features include: Internally Lubricated. |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM D790M |
DSM Somos® 7120 Epoxy Photopolymer, UV Postcure
(discontinued **) DescriptionDSM Somos® 7120 Photopolymer is a humidity-tolerant, high heat-deflection-temperature, low-curl, high-speed liquid that produces rigid, highly accurate parts. It produces exceptional, u.. |
|||
Flexural Strength | 108 MPa | 15600 psi | ASTM D790 |
Kolon DIAMAT® GP Description: DIAMAT® is a specially formulated high impact grade PMMA resin from KOLON. The acrylic composition results in an excellent balance of impact resistance and high modulus at reasonabl.. |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
Techmer ES HiFill® PA6 E U Availability: North AmericaForms: PelletsFeatures: General PurposeProcessing Method: ExtrusionTPCI# 9777102Information provided by TP Composites, Inc. |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
Techmer ES HiFill® PA6 HS L BK Heat Stabilized Availability: North AmericaForms: PelletsAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearance: BlackTPCI# 7190102Information provided by TP Composites, Inc. |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
Techmer ES Luriblend® PA6 E M/SL4 MB Availability: North AmericaForms: PelletsAdditive: Molybdenum Disulfide Lubricant and Silicone LubricantFeatures: Low Friction, Good Wear Resistance and LubricatedAppearance: BlackInformation provid.. |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
Techmer ES Luriblend® PA6 E ML2 MB Availability: North AmericaForms: PelletsAdditive: Molybdenum Disulfide LubricantFeatures: LubricatedAppearance: Natural ColorInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
Techmer ES Plastiblend® PA6 HS L MB Nylon 6 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer and LubricantHeat Stabilized and LubricatedTPCI# 7018102Information provided by TP Composites, Inc. |
|||
Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® GR-5020T SAN, 20% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® VB-4921 ABS, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® NF-3017H PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® GR-4020H ABS, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® GR-5020T SAN, 20% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GTX GTX679 PPE+PA6 (Asia Pacific) Noryl GTX* GTX679 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to al.. |
|||
Flexural Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GTX GTX679 PPE+PA6 Noryl GTX* GTX679 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to al.. |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
E-Polymers TEKAMID® TB120CR Fast Crystallinity PA6 Resin Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.T-series: Impact modified,.. |
|||
Flexural Strength | 108 MPa | 15700 psi | ISO 178 |
Cathay PA56 Renewable Engineering Polyamide, DAM Cathay engineering polyamides contain 26-100% renewably sourced material. Advantages: Operates at similar conditions to PA66; Suitable for injection, compounding and extrusion; Stable mechanical pr.. |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM Test |
BASF Ultramid® 8202 HS BK-102 PA6 (Dry) Ultramid 8202 HS BK-102 is an unfilled, heat stabilized, pigmented black, low viscosity, general purpose injection molding PA6 exhibiting excellent fluidity for filling thin sections. It possesses .. |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM Test |
BASF Ultramid® 8202 HS PA6 (Dry) Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose nylon 6 injection molding homopolymer. It possesses the combination of strength and toughness and has excellent chemical and ab.. |
|||
Flexural Strength | 108 MPa | 15700 psi | Wet; ASTM D790 |
Asahi Kasei Leona® 14G15 15% Glass Filled Nylon 66 15% Glass Fiber Reinforced. Enhanced strength and stiffnessApplications:Heater tanks, fuel injectors, ABS sensors, and other under-the-hood automotive parts Information provided by Asahi Kasei |
|||
Flexural Strength | 108 MPa | 15700 psi | Dry; ASTM D790 |
Asahi Kasei Leona® 9400S Nylon 66 Excellent impact resistance. Suitable for thick-wall parts.Applications:Railroad tie insulatorsInformation provided by Asahi Kasei |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
A. Schulman ComAlloy Aqualoy® 145 Polypropylene, Glass Reinforced, Chemically Coupled NSF Data provided by the manufacturer, ComAlloy International Company.40% Glass Reinforced. In Aqualoy® materials, carefully selected base resins and proprietary additives meld hydrolytic stability an.. |
|||
Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
Plaskolite West Optix® CA-61 General Purpose Acrylic Resin Injection Molding and Extrusion Grade Pellets. Good heat resistance, medium flow. |