BASF Ultradur® B 4300 G2 FC 10% Glass Filled PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultradur®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur® B 4300 G2 FC 10% Glass Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: The BASF Ultradur® FC (Food Contact) grades enable the industry to develop products for food contact applications which are in compliance with multiple regional food contact regulations including FDA.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.600 - 0.900 g/cc
0.0217 - 0.0325 lb/in³
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
ISO 62
Viscosity Measurement 115
115
[cm<sup>3</sup>/g]; ISO 307
Linear Mold Shrinkage, Flow 0.0070 cm/cm
0.0070 in/in
plate with film gate 150x150x3mm<sup>3</sup>
0.0122 cm/cm
0.0122 in/in
ISO 2577
Linear Mold Shrinkage, Transverse 0.0134 cm/cm
0.0134 in/in
plate with film gate 150x150x3mm<sup>3</sup>
0.0138 cm/cm
0.0138 in/in
ISO 2577
Melt Flow 21.92 g/10 min

@Load 2.16 kg,
Temperature 250 °C
21.92 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 160 MPa

@Load 98.0 kg,
Time 30.0 sec
23200 psi

@Load 216 lb,
Time 0.00833 hour
ISO 2039-1
Tensile Strength at Break 85.0 MPa
12300 psi
ISO 527-1/-2
Elongation at Break 4.5 %
4.5 %
ISO 524-1/-2
Tensile Modulus 4.50 GPa
653 ksi
ISO 527-1-2
Flexural Strength 140 MPa
20300 psi
ISO 178
Charpy Impact Unnotched 3.80 J/cm²

@Temperature -30.0 °C
18.1 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
4.00 J/cm²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²

@Temperature 23.0 °C
1.90 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 - 50.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
22.2 - 27.8 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/-2
Thermal Conductivity 0.230 W/m-K
1.60 BTU-in/hr-ft²-°F
DIN 52612-1
Melting Point 223 °C
433 °F
ISO 11357-1/-2
Maximum Service Temperature, Air 210 °C
410 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75-1/-2
Decomposition Temperature >= 290 °C
>= 554 °F
Flammability, UL94 HB

@Thickness >=0.400 mm
HB

@Thickness >=0.0157 in
IEC 60695-11-10
HB

@Thickness >=4.00 mm
HB

@Thickness >=0.157 in
by electrical sources of ignition, Method BH; IEC 60707
HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz
3.6

@Frequency 1.00e+6 Hz
IEC 60250
3.6

@Frequency 100 Hz
3.6

@Frequency 100 Hz
IEC 60250
Dissipation Factor 0.0012

@Frequency 100 Hz
0.0012

@Frequency 100 Hz
IEC 60250
0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 125 V
125 V
Test Solution B; IEC 60112
300 V
300 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
Injection molding/Extrusion
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Injection molding
Descriptive Properties Value Comments
Commercial Status Europe
Ignition Temperature 350°C
ASTM D1929