Styrolution Luran® S 767KE ASA
| Category | Polymer , Thermoplastic , ASA Polymer |
| Manufacturer | Styrolution |
| Trade Name | Luran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Luran® S 767KE ASA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Luran S 767KE is particular suitable for co-extrusion with PVC at low temperature. Hereby, it provides a glossy surface finish.Enhanced flowabilitySuitable for co-extrusion with PVCEnables high gloss surface in extrusionInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.35 % @Temperature 23.0 °C |
0.35 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 1.65 % @Temperature 23.0 °C |
1.65 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | ISO 294-4 |
| Melt Flow | 17 g/10 min @Load 10.0 kg, Temperature 220 °C |
17 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 80.0 MPa | 11600 psi | ISO 2039-1 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 - 110 µm/m-°C | 44.4 - 61.1 µin/in-°F | ISO 11359 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75 |
| Vicat Softening Point | 98.0 °C @Load 5.10 kg |
208 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 105 °C @Load 1.02 kg |
221 °F @Load 2.25 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
IEC 60250 |
| Dissipation Factor | 0.011 @Frequency 100 Hz |
0.011 @Frequency 100 Hz |
IEC 60250 |
| 0.024 @Frequency 1.00e+6 Hz |
0.024 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | ISO 294 |
| Mold Temperature | 60.0 °C | 140 °F | ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 41 UVT LL General Purpose Acrylic Resin
- MV Labs RE450 K2ReCl6 Potassium hexachlororhenate(IV)
- Plaskolite West Optix® CP - 81 General Purpose Acrylic Resin
- Lavergne VYPET VNT 1021 Polyester-PC Alloy
- Techmer ES Plaslube® J-1/CF/10/TF/20 BK PA66
- Samsung Cheil Industries Starex® AS-0151BS ABS, Unreinforced
- Sumitomo Bakelite North America E 9405H-1 Glass Filled Electrical Encapsulation Grade Epoxy
- Adell AH-38 Nylon 66, 40% Mineral Filled
- Barlog Plastics KEBAFORM C 908 EL POM Copolymer unreinforced, impact modified
- BCC Products BC 9060 Silicone RTV Rubber
Copyright © lookpolymers.com All Rights Reserved