- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 97.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 97.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ASTM D648 |
| Plaskolite West Optix® CA-71 General Purpose Acrylic Resin Injection Molding and Extrusion Grade Pellets. High heat resistance, medium flow. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C @Thickness 3.17 mm |
207 °F @Thickness 0.125 in |
ASTM D648 |
| Covestro Bayblend® 2153 Polycarbonate + ABS Blend, General Purpose
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ASTM D648 |
| LG Chemical Lupox® PBT-HI1002FM Impact Modified, Flame Retardant PBT Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C @Thickness 6.35 mm |
207 °F @Thickness 0.250 in |
ASTM D648 |
| IRPC Polimaxx Porene KU200 Acrylonitrile Butadiene Styrene Applications:extrusion applicationautomotive parts such as instrument panels, console boxes, switches, automotive louvers, ectelectrical appliances |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75A |
| Lucite International Diakon® Frost 902 51 Acrylic Polymer Information provided by Lucite International |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Xenoy® X4830 PBT+PC (Europe-Africa-Middle East) Xenoy X4830 is a hydrostable, high modulus, low temperature ductile PC/PBT blend. Furthermore, this resin provides high chemical resistance, very low creep, low CTE, excellent fatique and high heat .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp AF0029 ABS LNP* Thermocomp* AF0029 is an ABS base resin containing Glass Fiber. Characteristics of this grade are Flame Retardancy.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp AF0029 ABS LNP* Thermocomp* AF0029 is an ABS base resin containing Glass Fiber. Characteristics of this grade are Flame Retardancy.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp FF008L PE LNP* Thermocomp* FF008L is a compounding based on Polyethylene containing glass fiber. Added characteristics include Low Extractible.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | annealed; ASTM Test |
| Styrolution Luran® S 777 K ASA Luran S 777 K is an easy flowing injection molding ASA grade with good toughness and heat distorsion resistance. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75 |
| Styrolution Terluran® HI-12 ABS Terluran HI-12 is an injection molding grade of ABS with a very high toughness and easy flow.Very high toughnessEasy flowingUL 94 HB (1.6 & 3.2 mm)Information provided by Styrolution |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C @Thickness 6.40 mm |
207 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® NH-0300 ABS, Unreinforced FR Flame-retardant non-halogen ABS with superior heat resistance that can be used in the interior/exterior material of CD/DVD-Combo and DVD-RecordersInformation provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP SH0430AC_BK1D466 PA12 4.3 specific gravity nylon 12, clean compound system |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ASTM D648 |
| Shinkong Synthetic Fibers Shinite® D201M20 PBT, 20% Mineral Filled Information from Shinkong Synthetic Fibers Corp. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Annealed; ISO 75-2/A |
| Styron MAGNUMâ„¢ 3904 Acrylonitrile Butadiene Styrene (ABS) Resin Overview: MAGNUMâ„¢ 3904 is a resin with super-high impact. It is used in a wide range of technical applications. It can be processed by injection molding, extrusion or thermoforming. The mass (c.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Annealed; ISO 75-2/A |
| Styron MAGNUMâ„¢ 3904 Smooth Acrylonitrile Butadiene Styrene (ABS) Resin Overview: MAGNUMâ„¢ 3904 is an extrusion/thermoforming resin developed for high impact and other technical applications. The mass (continuous process) ABS technology of Styron ensures an ABS tech.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Xenoy® XLG2400 PC+PET Low Gloss Xenoy, providing inherent low gloss on almLow Gloss Xenoy, providing inherent low gloss on almost every type of tool surfaces. This grade has excellent low temperature impact, high heat re.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | 0.5 inch unannealed; ASTM D648 |
| PlastxWorld CEVIAN® SERG2 20% GF ABS Glass fiber reinforced and flame retarded ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | 0.5 inch unannealed; ASTM D648 |
| PlastxWorld CEVIAN® SERG3 30% GF ABS Glass fiber reinforced and flame retarded ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75-1/-2 |
| Covestro Bayblend® T50 XF Polycarbonate + ABS Injection molding gradeVicat/B 120 = 115 °Cexcellent flowgood low temperature impact strengthPreprocessingMax. Water content |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 100PE BK602 Acetal (POM)
(Unverified Data**) High Viscosity Acetal Homopolymer with Very Low Emissions Delrin 100PE BK602 (formerly DE20573) is a high viscosity acetal homopolymer an enhanced version of Delrin 100P with very low VOC emissions... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 500AL NC010 Acetal (POM)
(Unverified Data**) Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Delrin 500AL is a medium viscosity acetal homopolymer with an advanced system of lubrication for applications requiring .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75 |
| Azoty Tarnow™ TARNOFORM 300 HI2 POM Rubber modified grade with very high impact strength and damping capacity.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C @Thickness 6.40 mm |
207 °F @Thickness 0.252 in |
Method A; ASTM D648 |
| Bhansali Engineering Abstron HI40H ABS Injection Molding Grade Automotive applications -Medium Impact, Super High Rigidity, PaintableInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron HR-59 ABS Heat Resistant High, Medium Impact Heat Resistant Grades with good flowInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C @Thickness 6.40 mm |
207 °F @Thickness 0.252 in |
Method A; ASTM D648 |
| Bhansali Engineering Santron IMS 2006 SAN Resin Very High Rigidity Clear SANInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75 |
| Ineos Nova 202W Crystal Polystyrene High Heat Extrusion Grade
(discontinued **) Excellent heat resistance, Superior melt strengthApplications: Foam insulationProperties were determined on injection molded specimens at 23° and 50% RH unless otherwise specified.Information provi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C @Thickness 6.40 mm |
207 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON Noryl_FMC1010 PPE+PS LNP* Stat-kon* Noryl_FMC1010 compound is a 10% carbon fiber, static dissipative, foamable resin Nonchlorinated, nonbrominated. UL94 V1 rated. Property values at 20% WR, 0.250"" wall. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C @Thickness 6.40 mm |
207 °F @Thickness 0.252 in |
Method A; ASTM D648 |
| Bhansali Engineering Abstron HI40H ABS Injection Molding Grade Automotive applications -Medium Impact, Super High Rigidity, PaintableInformation provided by Bhansali |
|||