PolyOne Lubri-Tech™ ATH-5KV/000 Acetal-Homopolymer, Aramid Fiber (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ ATH-5KV/000 Acetal-Homopolymer, Aramid Fiber
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Aramid Fiber ReinforcedInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Water Absorption | 0.050 % @Thickness 3.17 mm |
0.050 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.020 - 0.025 cm/cm | 0.020 - 0.025 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.2 MPa | 8000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.76 GPa | 400 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 55.2 MPa | 8000 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 265 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | Unannealed, 0.125 in bars; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Nymax™ 1200 A HS Natural A Polyamide 66 (Nylon 66)
- Qualchem Danamid FEW-25 Polyamide 6, 25% Mineral Filled
- ExxonMobil LD 051.LT Shrink Film Resin (discontinued **)
- LATI Later 4 G/30-V0CT2 PBT, 30% Glass Fiber Reinforced, Flame Retardant
- A. Schulman PAPERMATCH® T-4228-50 Specialty Masterbatch
- ExxonMobil 150 Mobil DTE PM Series
- Axiall 16640 Wire & Cable Flexible PVC
- Axiall 6652 Moldings & Extrusions Flexible PVC
- Abatron AboCast/AboCure 4-4/50-3 Casting Epoxy for Tooling
- Lehmann & Voss LUVOCOM® 1105-8344/GY PEEK, unreinforced
Copyright © lookpolymers.com All Rights Reserved