Polykemi AB POLYform POM C M90 GF10 Polyoxymethylene
| Category | Polymer , Thermoplastic |
| Manufacturer | Polykemi AB |
| Trade Name | POLYform |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYform POM C M90 GF10 Polyoxymethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Filler Content | 10 % | 10 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0090 - 0.014 cm/cm | 0.0090 - 0.014 in/in | With Flow; ISO 2577 |
| 0.0090 - 0.014 cm/cm | 0.0090 - 0.014 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 70.0 MPa | <= 10200 psi | ISO/R527 |
| Elongation at Break | 7.0 % | 7.0 % | ISO/R527 |
| Flexural Strength | <= 105 MPa | <= 15200 psi | ISO 178 |
| Flexural Modulus | 4.00 GPa @Temperature 23.0 °C |
580 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 155 °C @Load 5.001 kg |
311 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- PSM Industries Pacific Sintered Metals Infiltrated High Carbon Steel FX-232-T(HT) Powdered Metal
- PolyOne Geon™ Vinyl Fittings M1005 Polyvinyl Chloride, Rigid (PVC, Rigid)
- LNP VALOX® SMV5845 PBT + PET Alloy, 16% Carbon Fiber Reinforcement (discontinued **)
- Jackon JACKOCELL® R312 Expanded Polystyrene Packaging and Shape Molding
- Saint-Gobain Chemfab® q-GUARD® 35 Insulation Jacketing
- Samsung Cheil Industries Starex® SG-101 Expandable Polystyrene (EPS) High Expansion
- Hexcel® Redux® 322 Modified epoxy film adhesive (0.078 psf)
- CoorsTek Boron Carbide Reaction-Bonded Boron Carbide
- CP-Polymer-Technik Wellamid® 6000 MRGV 20/10 HWCP 20% Mineral and 10% Glass Fiber Nylon 6, Heat Stabilized, Dry
Copyright © lookpolymers.com All Rights Reserved