- Polymer Property : Melt Flow = 17 g/10 min
Polymer Property : Melt Flow = 17 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products F4702-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Exterior door moldingsRigid bumper coversInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 17 g/10 min @Load 0.325 kg, Temperature 270 °C |
17 g/10 min @Load 0.716 lb, Temperature 518 °F |
|
| Plastcom SLOVALEN PH 71 T 20 PP, 20% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 20% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shr.. |
|||
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products FT4650-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Scuff platesExterior grillesBodyside moldingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products FT4650-01UV Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Scuff platesExterior grillesBodyside moldingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products FT4700-00A Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: CladdingsBodyside moldingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products FT4900-745UV Thermoplastic Polyolefin, UV Stabilized, CJM Medium Khaki Solid Applications: Exterior componentsBodyside moldingsStep padsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products T20P104-01 20% Talc Reinforced Polypropylene, Black Applications: Electronic housingsIP componentsHVAC ducts - air distributionClose out panelDurable goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 17 g/10 min @Load 1.20 kg, Temperature 300 °C |
17 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| SABIC Innovative Plastics Lexan® 1173X PC Copolymer (Europe-Africa-Middle East) Lexan* 1173X polycarbonate (PC) resin is a high flow, UV stabilized injection molding grade. This resin offers good low temperature (-30 C) ductility in combination with high flow characteristics an.. |
|||
| Melt Flow | 17 g/10 min @Load 1.20 kg, Temperature 300 °C |
17 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Ravago Manufacturing Americas Hylex® P1017L Polycarbonate, Unreinforced, High Flow, Mold Release Information provided by Ravago. |
|||
| Melt Flow | 17 g/10 min @Load 1.20 kg, Temperature 300 °C |
17 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Ravago Manufacturing Americas Hylex® P1317L Polycarbonate, UV Stabilized, Higher Flow, Mold Release Information provided by Ravago. |
|||
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 190 °C |
17 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| NOVA Chemicals Sclair® 2710 HDPE Injection Molding Resin Features: Good ESCR, good processability.Applications: Housewares, containers, toys.Data provided by the manufacturer. |
|||
| Melt Flow | 17 - 23 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 - 23 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Ineos H20SLME Polypropylene Homopolymer This is a homopolymer designed for injection molding, and it is compliant with both the FDA status and the EU Food Contact status.Information provided by Ineos Olefins & Polymers USA |
|||
| Melt Flow | 17 - 23 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 - 23 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Ineos H20YLME Polypropylene Homopolymer This is a homopolymer designed for injection molding, and it is compliant with both the FDA status and the EU Food Contact status.Information provided by Ineos Olefins & Polymers USA |
|||
| Melt Flow | 17 - 23 g/10 min @Load 2.16 kg, Temperature 190 °C |
17 - 23 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
| Ipiranga Petrochem HA 7260 HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce .. |
|||
| Melt Flow | 17 g/10 min @Load 10.0 kg, Temperature 250 °C |
17 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® TH-1100 PC, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238; ISO 1133 |
| Styron INSPIREâ„¢ TF1301 Thermoplastic Polyolefin Information provided by DowThe Inspire brand was spun off from Dow Chemical to Styron in 2010 |
|||
| Melt Flow | 17 g/10 min @Load 5.00 kg, Temperature 200 °C |
17 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Supreme Petrochem SP6433 9710 Medium Impact Polystyrene Characteristics High flow Good toughness Good shine Available in various colors Processing Injection molding Extrusion Applications Pipes & profiles for wiring Beading for furniture and tables .. |
|||
| Melt Flow | 17 - 23 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 - 23 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 1329H-01 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1329H-01 is a natural high flow, medium impact polypropylene that is suitable for molding thin parts with long mold flow distances. It permits reduction of injection tem.. |
|||
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| A. Schulman POLYFORT™ FPP 1697HU High Flow Fortified Polypropylene DescriptionPolyfort® FPP 1697HU is a high flow fortified polypropylene with high temperature dimensioned stability. It is stabilized for UV exposure and available in matched automotive color.Infor.. |
|||
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 190 °C |
17 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Yellow 2200 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 2200 is a yellow color concentrate based in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 2200 contai.. |
|||
| Melt Flow | 17 - 23 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 - 23 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 1467-01 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1467-01ApplicationPP 1467-01 meet FDA Regulation 21 CFR 177.1520, for all food contact applications.Information provided by A. Schulman. |
|||
| Melt Flow | 17 g/10 min @Load 1.20 kg, Temperature 300 °C |
17 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Cossa Polimeri ESTACARB 1601 OPALE Polycarbonate Polycarbonate for injection moldingOpal, light diffusiveInformation provided by Cossa Polimeri S.r.l. |
|||
| Melt Flow | 17 g/10 min @Load 5.00 kg, Temperature 260 °C |
17 g/10 min @Load 11.0 lb, Temperature 500 °F |
|
| Covestro Bayblend® T 44 Polycarbonate/ABS Blend Easier flowing than BAYBLEND T 45 MN.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
| Melt Flow | 17 g/10 min @Load 1.20 kg, Temperature 300 °C |
17 g/10 min @Load 2.65 lb, Temperature 572 °F |
estimated from MVR using room temperature density; ISO 1133 |
| Covestro Makrolon® 2558 Polycarbonate ISO 7391-PC,MR,(,,)-18-9MVR (300 °C/1.2 kg) 14.5 cm3/10 minMedical devicessuitable for ETO and steam sterilization at 121 °CComplies with the requirements of FDA-modified ISO 10993-1 and USP Class.. |
|||
| Melt Flow | 17 g/10 min @Load 1.20 kg, Temperature 300 °C |
17 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Entec Hylex® P1017L1 HB Polycarbonate Available in North America Additive: Mold Release Features: Good Mold Release and High Flow RoHS Compliant Form: Pellets Appearance: Clear/Transparent Information provided by Entec |
|||
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| ExxonMobil PP7054L1 Polypropylene Impact Copolymer Product Description: A nucleated impact copolymer resin with medium flow. It is suitable for molding applications like consumer products, closures, containers, toys and rigid packaging applications.. |
|||
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 190 °C |
17 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| DuPont Performance Polymers Delrin® FG400MTD BLA079 Acetal (POM)
(Unverified Data**) Metal Detectable Medium Viscosity Acetal Copolymer Developed for Food Contact Applications Delrin FG400MTD BLA079 is a metal filled medium viscosity acetal copolymer for injection molding. It is det.. |
|||
| Melt Flow | 17 g/10 min | 17 g/10 min | ASTM D1238 |
| Aclo Accutech Polypropylene Copolymer CP0437W20L Wollastonite Reinforced |
|||
| Melt Flow | 17 g/10 min | 17 g/10 min | ISO 1133 |
| Addiplast Addilene J 470 ST14 Polypropylene Copolymer Soft touchInformation provided by Addiplast. |
|||