Styrolution Luran® S 757 R Colored ASA
| Category | Polymer , Thermoplastic , ASA Polymer |
| Manufacturer | Styrolution |
| Trade Name | Luran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Luran® S 757 R Colored ASA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: General-purpose grade for injection molding with high stiffness.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Water Absorption | 1.65 % | 1.65 % | Equilibrium; ISO 62 |
| 0.45 % @Time 86400 sec |
0.45 % @Time 24.0 hour |
ISO 62 | |
| Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | 23°C/50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 8.56 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.56 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 100 MPa @Load 36.5 kg, Time 30.0 sec |
14500 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527-1/-2 |
| Elongation at Break | 8.0 % | 8.0 % | Nominal, 50 mm/min; ISO 527-1/-2 |
| Elongation at Yield | 3.1 % | 3.1 % | 50 mm/min; ISO 527-1/-2 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ISO 527-1/-2 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Poissons Ratio | 0.44 | 0.44 | Calculated |
| Shear Modulus | 0.900 GPa | 131 ksi | ISO 6721-2 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 20.0 J/cm² @Temperature 23.0 °C |
95.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1000 hours | 1400 MPa @Strain <=0.500 % |
203000 psi @Strain <=0.500 % |
ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 - 110 µm/m-°C @Temperature 23.0 - 80.0 °C |
44.4 - 61.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Maximum Service Temperature, Air | 85.0 °C | 185 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75-1/-2 |
| Vicat Softening Point | 98.0 °C | 208 °F | VST/B/50; ISO 306 |
| 105 °C | 221 °F | VST/A/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Diameter 4.00 mm |
HB @Diameter 0.157 in |
IEC 60707 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | K20/P20; IEC 60243-1 |
| Dissipation Factor | 0.0090 @Frequency 100 Hz |
0.0090 @Frequency 100 Hz |
IEC 60250 |
| 0.025 @Frequency 1.00e+6 Hz |
0.025 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Test Liquid A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | Injection |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection |
| Drying Temperature | 80.0 °C | 176 °F | Pre-drying |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Pre-drying |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Beige 36598 Q42 | |
| Black 56625 | ||
| Black 71200 | ||
| Black Q427 | ||
| Gray 00302 | ||
| Natural | ||
| White 25820 Q 438 | ||
| White 31718 | ||
| White 34858 | ||
| White 36304 Q35 | ||
| White 36327 | ||
| White 36448 | ||
| Commercial Status | Europe | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 6.0 PHR MBTS
- Phillips 66 COPYLENE® CH085S Polypropylene, Homopolymer, Cast Film, Slip
- Fine Organics FINALUX G 301 Lubricant Additive
- Schott Glass 8242 Borosilicate Glass
- Topas Advanced Polymers TOPAS® 6013S-04 Cyclic Olefin Copolymer (COC)
- CTC X-PRO PP 2021 Polypropylene Impact Copolymer
- Devcon Plastic Steel® Putty (A) Epoxy
- DuPont Teijin Films Mylar® MO21 Polyester Film, 750 Gauge
- 3M 4508 Single-Coated Foam Tape
- E-Polymers SEPAZ® K130HF 30% Glass Fiber Reinforced High Flow PPS Resin
Copyright © lookpolymers.com All Rights Reserved