Lanxess Durethan® BKV 130 DUS008 901510 Nylon 6, Glass Fiber Reinforced, Impact Modified

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Filled, Impact Grade
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 130 DUS008 901510 Nylon 6, Glass Fiber Reinforced, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, 30% glass fibers, injection molding, impact modifiedInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.37 g/cc
1.37 g/cc
ISO 1183
Moisture Absorption at Equilibrium 1.9 %
1.9 %
50% RH; ISO 62
Water Absorption at Saturation 6.3 %
6.3 %
ISO 62
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0030 cm/cm
0.0030 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0020 cm/cm
0.0020 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0070 cm/cm
0.0070 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 95.0 MPa
13800 psi
cond.; ISO 527-1, -2; 5 mm/min
155 MPa
22500 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 3.5 %
3.5 %
d.a.m.; ISO 527-1, -2; 5 mm/min
7.5 %
7.5 %
cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 5.20 GPa
754 ksi
cond.; ISO 527-1, -2; 1 mm/min
9.30 GPa
1350 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 160 MPa

@Strain 6.30 %
 23200 psi

@Strain 6.30 %
 cond., 2 mm/min; ISO 178-A
245 MPa

@Strain 4.00 %
 35500 psi

@Strain 4.00 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 135 MPa

@Strain 3.50 %
 19600 psi

@Strain 3.50 %
 cond., 2 mm/min; ISO 178-A
240 MPa

@Strain 3.50 %
 34800 psi

@Strain 3.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 4.70 GPa
682 ksi
cond., 2 mm/min; ISO 178-A
8.60 GPa
1250 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1A
12.0 kJ/m²

@Temperature 23.0 °C
 5.71 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1A
20.0 kJ/m²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1A
Izod Impact, Unnotched (ISO) 70.0 kJ/m²

@Temperature -30.0 °C
 33.3 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
70.0 kJ/m²

@Temperature -30.0 °C
 33.3 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1U
80.0 kJ/m²

@Temperature 23.0 °C
 38.1 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
85.0 kJ/m²

@Temperature 23.0 °C
 40.4 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1U
Charpy Impact Unnotched 7.00 J/cm²

@Temperature -30.0 °C
 33.3 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
7.50 J/cm²

@Temperature -30.0 °C
 35.7 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eU
9.00 J/cm²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
9.00 J/cm²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eU
Puncture Energy 2.60 J

@Load <=76.5 kg,
Temperature -30.0 °C
 1.92 ft-lb

@Load <=169 lb,
Temperature -22.0 °F
 ISO 6603-2
4.00 J

@Load <=94.8 kg,
Temperature 23.0 °C
 2.95 ft-lb

@Load <=209 lb,
Temperature 73.4 °F
 ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 11.1 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature 23.0 - 55.0 °C
 55.6 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75-1, -2
Vicat Softening Point 213 °C

@Load 5.10 kg
 415 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F
280 °C
536 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6-HI, GR, 14-090, GF30