Polymer Property : Ball Indentation Hardness = 100 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	100 MPa	14500 psi	ISO2039.1 DIN.53456
Omnia Plastica Akulon® PA 66 - Akulon 66 - at 50% RH Polyamide obtained by the polymerisation of Hexamethylenediamine and Adipic acid. It is one of the oldest engineering plastics, having been created in the USA in 1930. Due to its origin it is widely..
Ball Indentation Hardness	100 MPa	14500 psi	ISO2039.1 DIN.53456
Omnia Plastica Akulon® PA 66.6 - Akulon GX - at 50% RH Copolymer of nylon with excellent mechanical features, it combines the good impact resistances of PA6 as well as the higher stiffness of PA66. For this reason it machines very well on automatic tool..
Ball Indentation Hardness	100 MPa	14500 psi	ISO2039.1 DIN.53456
Omnia Plastica PA 11 Rilsan B The only engineering plastic of natural origin (derived from castor oil), it is a polyamide which, unlike the other nylons, does not absorb humidity. It has all the good mechanical features of polya..
Ball Indentation Hardness	100 MPa	14500 psi	ISO 2039-1
Nilit FRIANYL A63 S20 Nylon 6.6 for injection molding Nylon 6.6 for injection molding, impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	100 MPa	14500 psi	ISO 2039-1
Nilit FRIANYL B63 L-HS-GV30 Nylon 6 for injection molding, 30% glass fiber reinforced Nylon 6 for injection molding, improved fluidity, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	100 MPa	14500 psi	ISO 2039-1
Nilit FRIANYL B63 S20 Nylon 6 for injection molding Nylon 6 for injection molding, impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	100 MPa	14500 psi	DIN 53456
Ineos Nova S-3401 Medium Impact Compact Polystyrene (discontinued **) Impact polystyrene with good flow characteristics and a high elongation. Generally used for applications where a tough material is required. The material is provided with external lubricate to imp..
Ball Indentation Hardness	100 - 325 MPa	14500 - 47100 psi	Average value: 223 MPa Grade Count:21
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl..
Ball Indentation Hardness	100 - 135 MPa	14500 - 19600 psi	Average value: 122 MPa Grade Count:3
Overview of materials for Nylon 12, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of ..
Ball Indentation Hardness	100 MPa	14500 psi	ISO 2039-1
Ineos ABS LustranÂ® Ultra 4000 PG ABS Pellets (a-methylstyrene-SAN-modified), Electroplating Grade LustranÂ® Ultra 4000 PG is electroplating grade with high heat resistance. It is used for the production of molded plastic articles.
Ball Indentation Hardness	100 MPa	14500 psi	ISO 2039-1
Ineos ABS LustranÂ® Ultra 4115 ABS Pellets (a-methylstyrene-SAN / PC-modified), Very High Heat Grade LustranÂ® Ultra 4115 is very high heat grade with high impact resistance and is PC-modified. It is used for the production of molded plastic articles.
Ball Indentation Hardness	100 MPa	14500 psi	Hc 30; ISO 2039; partially
Schwartz Technical Plastics LAMIGAMIDÂ® 200 Polyamide 66, Conditioned Application: bearing bushes, machine parts, gears, linersInformation provided by Schwartz Technical Plastics GmbH
Ball Indentation Hardness	100 MPa @Load 36.5 kg, Time 30.0 sec	14500 psi @Load 80.5 lb, Time 0.00833 hour	ISO 2039-1
Styrolution LuranÂ® S 757 R Colored ASA Description: General-purpose grade for injection molding with high stiffness.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
Ball Indentation Hardness	100 MPa	14500 psi	ISO 2039-1
Styrolution NovodurÂ® 4000PG ABS Novodur Ultra 4000PG is an injection molding grade especially suitable for electroplating, providing enhanced heat resistance.Information provided by Styrolution
Ball Indentation Hardness	100 MPa	14500 psi	ISO 2039-1
Styrolution NovodurÂ® 5300 ABS Novodur 5300 is a high heat injection molding grade with high impact strength, good chemical resistance and reduced emission (PC modified)Information provided by Styrolution
Ball Indentation Hardness	100 MPa	14500 psi	DIN 53456
Zell-Metall Engineering Plastics Zellamid 1200 G Zellamid® 1200 G is manufactured by an activated anionic reaction. Finished and semi-finished parts are produced by a static cast process. This process makes it possible to produce a material wit..
Ball Indentation Hardness	100 MPa	14500 psi	H 358/30; ISO 2039; DIN 53456
Zell-Metall Engineering Plastics Zellamid 250 (PA6.6) at 50% RH Zellamid® 250 is noted for its high temperature resistance and high tensile strength. It is the hardest and most rigid type of extruded Nylon. Main characteristics are high resistance to fuels, oil..
Ball Indentation Hardness	100 MPa	14500 psi	conditioned; ISO 2039-1
EMS-Grivory Grivory® BG-30/2 PA6-GF30 Product description: Grilon BG-30/2 is a heat stabilized, normal viscosity PA6 injection molding grade with 30% glass fibers. Grilon BG-30/2 has the following important properties: High stiffnessGoo..
Ball Indentation Hardness	100 MPa	14500 psi	conditioned; ISO 2039-1
EMS-Grivory Grivory® TSG-35 PA666-GF35 Information provided by EMS Grivory
Ball Indentation Hardness	100 MPa	14500 psi	dry; ISO 2039-1
EMS-Grivory Grivory® XE 4071 black 9992 PA612 Product description: Grilamid XE 4071 BLACK 9992 is an impact modified unreinforced high viscosity polyamide 612 (PA612) extrusion grade with superior heat and hydrolysis resistance. Compared to sta..
Ball Indentation Hardness	100 MPa	14500 psi	dry; ISO 2039-1
EMS-Grivory Grivory® XE 4188 black 9992 PA612 Product description: Grilamid XE 4188 black 9992 is a high viscosity, unreinforced, impact resistant polyamide 612 (PA612) extrusion grade. Unique features of Grilamid XE 4188 black 9992 are: High v..
Ball Indentation Hardness	100 MPa	14500 psi	dry; ISO 2039-1
EMS-Grivory Grivory® XE 4188 nat PA612 Product description: Grilamid XE 4188 natural is a high viscosity, unreinforced, impact resistant polyamide 612 (PA612) extrusion grade. Unique features of Grilamid XE 4188 natural are: High viscosi..
Ball Indentation Hardness	100 MPa	14500 psi	conditioned; ISO 2039-1
EMS-Grivory Grivory® XE 5026 (BG-30 H) PA6-GF30 Product description: Grilon B XE 5026 (BG-30 H) black 9922 is a high heat stabilized, 30% glass fiber reinforced PA6- Injection molding grade with modified flowability. Grilon B XE 5026 (BG-30 H) bl..
Ball Indentation Hardness	100 MPa	14500 psi	H358/30; ISO 2039-1
Chi Mei Wonderlite® PC-110V Polycarbonate - Flame Retardant
Ball Indentation Hardness	100 - 170 MPa @Time 30.0 sec	14500 - 24700 psi @Time 0.00833 hour	DIN 53 456
Hippe PA 66 Nylon 66 The polyamide with high degree of hardness, stiffness, scuff strength and stability of shape under heat. Preferred polyamide for components subjected to high load and heat stress in electrical, mec..
Ball Indentation Hardness	100 MPa	14500 psi	H358/30; ISO 2039-1
Chi Mei Wonderlite® PC-110N Polycarbonate - Flame Retardant Opaque
Ball Indentation Hardness	100 MPa	14500 psi	value at 30 sec.; ISO 2039-1
CENTROPLAST CENTROPHEN Polyphenylene ether modified This material is a lightweight plastic with low moisture absorption, and is impact resistant at low temperatures. Applications include fittings, drive components for domestic appliances, and compon..
Ball Indentation Hardness	100 MPa @Time 30.0 sec	14500 psi @Time 0.00833 hour	DIN 53 456
Hippe PVC-U Polyvinyl Chloride Material at reasonable price, high strength. Used in machine construction as covers, pipes, section, façade elements.Information provided by Hippe.
Ball Indentation Hardness	100 - 175 MPa	14500 - 25400 psi	Average value: 149 MPa Grade Count:8
Overview of materials for Acrylic, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Extruded". Each property range of values reported is minimum and maximum values of appropriate ..
Ball Indentation Hardness	100 MPa	14500 psi	conditioned; ISO 2039-1
EMS-Grivory Grivory® LC-15H black PA12-CF15 Product description: Grilamid LC-15H black is a Polyamide 12 injection molding product reinforced with 15% carbon fibers. The product is inherently black and is only available in this color.Main Att..