Braskem H 117 Injection Molding Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer	Braskem
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Braskem H 117 Injection Molding Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: H 117 is a ultra-high melt flow rate homopolymer. This product is suitable to high productivity on thin-walled parts. H 117 features an excellent stiffness, thermal resistance, low warpage parts, easy mould filling and high speed injection moulding.Applications: Thin-walled parts; Media Packaging; Housewares. Information provided by Braskem

Physical Properties	Metric	English	Comments
Density	0.905 g/cc	0.0327 lb/in³	ASTM D792A
Melt Flow	45 g/10 min @Load 2.16 kg, Temperature 230 °C	45 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238L

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	105	105	ASTM D785
Tensile Strength, Yield	38.0 MPa	5510 psi	ASTM D638
Elongation at Yield	9.0 %	9.0 %	ASTM D638
Flexural Modulus	1.60 GPa	232 ksi	ASTM D790
Izod Impact, Notched	0.200 J/cm @Temperature 23.0 °C	0.375 ft-lb/in @Temperature 73.4 °F	ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	123 °C	253 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	65.0 °C	149 °F	ASTM D648
Vicat Softening Point	155 °C	311 °F	-1kg; ASTM D1525