- Acrylonitrile Butadiene Styrene (ABS), Extruded
- Samsung Cheil Industries Starex® SV-0167EX Extrusion Grade ABS
Samsung Cheil Industries Starex® SV-0167EX Extrusion Grade ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SV-0167EX Extrusion Grade ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 99 | 99 | ASTM D785 |
| Tensile Strength, Yield | 40.0 MPa @Thickness 3.17 mm |
5800 psi @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 57.9 MPa @Thickness 3.17 mm |
8400 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 1.93 GPa @Thickness 3.17 mm |
280 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 4.81 J/cm @Thickness 3.17 mm |
9.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 6.35 mm |
194 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | Unannealed; ISO R 306 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 200 - 220 °C | 392 - 428 °F | |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |
| Front Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Nozzle Temperature | 230 - 250 °C | 446 - 482 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 68.9 - 82.7 MPa | 10000 - 12000 psi | |
| Back Pressure | 0.689 - 1.38 MPa | 100 - 200 psi | |
| Shot Size | 50 - 80 % | 50 - 80 % | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Processing Fill Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Q70W Polyurethane Rubber
- Polykemi AB POLYfill PPH GF1030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- NIZHNEKAMSKNEFTEKHIM PE 4148B (484H2) High Density Polyethylene
- SABIC Innovative Plastics LNP LUBRICOMP WI001 PBT
- Shandong Rike Chemical HELIâ„¢ HL-230P PVC Processing Aid Series (PA)
- Teknor Apex Telcar® TL-2530F Thermoplastic Elastomer
- Unitika E-RUNG60 Ultra high-rigidity PA6, Dry
- Polyplastics Duracon® M270-44/M270S Acetal Co-polymer (POM), Standard, High flow, High cycle
- Fiberfil® J-68/20/E Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled
Copyright © lookpolymers.com All Rights Reserved