Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 40.0 MPa | 5800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® S702 ABS (Europe-Africa-Middle East) CYCOLAC S702 is a high impact ABS combined with a good flow. This material is developed for enclosures and housings found in appliances and automotive industries.This data was supplied by SABIC-IP f.. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics GELOY CR8510 ASA ASA with outstanding UV exposure performance for both exterior and interior applications. F1 Rated. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics GELOY CR7500 ASA (Europe-Africa-Middle East) High heat ASA with optimum flow-impact balance. For Automotive applications and Automotive colors only. |
|||
Tensile Strength, Yield | 40.0 - 82.0 MPa | 5800 - 11900 psi | Average value: 53.2 MPa Grade Count:11 |
Overview of materials for Acetal Copolymer, Steel Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Steel Filled". Each property range of values reported is minimum and maximum values of.. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM D638 |
Gichem GILAC F120 Acrylonitrile Butadiene Styrene
(discontinued **) ABS high fluidity, good stiffness and excellent stampability. Medium-High Injection speed.Information provided by GICHEM Gruppo Industriale Chimico |
|||
Tensile Strength, Yield | 40.0 - 70.0 MPa | 5800 - 10200 psi | Injection; ISO 527 |
Raschig Group RALUPOL® 8602 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic molding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical streng.. |
|||
Tensile Strength, Yield | 40.0 - 70.0 MPa | 5800 - 10200 psi | Injection; ISO 527 |
Raschig Group SURAPLAST 54 UPA Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for.. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | |
Ineos ABS Centrex® 815 ASA Blend
(discontinued **) Key Features:UnfilledLight stabilized or stable to lightU.V. stabilized or stable to weatherHeat stabilized or stable to heatSuitable processing methods:Injection moldingInformation provided by Baye.. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM D638 |
Flint Hills P4G4K-205 Homopolymer Polypropylene Features: Clarified material. Product does not contain animal derived components. Phthalate-free.Applications: Cast FilmInformation provided by Flint Hills Resources. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527 |
GEHR Plastics PVDF-ELS Polyvinylidene Fluoride, Electrically Conductive Polyvinylidene fluoride shows a higher tensile strength, pressure resistance and dimensional stability than the related PTFE, but friction and insulation properties are lower. PVDF has a high mechan.. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM D638 |
Global ABS-501 High Impact Extrusion Grade ABS Information provided by Global Polymers Corporation. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527 |
Solvay Technyl® B 50H1 Nylon 66/6, Flame Retardant, EH50 Flame retardant copolyamide 66/6, unreinforced, heat stabilized, for injection molding.This phosphorus and halogen free flame retardant grade, UL 94 VO (0.4 mm), offers excellent filling qualities a.. |
|||
Tensile Strength, Yield | >= 40.0 MPa | >= 5800 psi | 50mm/min; ASTM D638 |
Shanghai Ofluorine Z-1 PVDF Injection Grade Description: Z-1 PVDF is a kind of granular homopolymer, which has low melt viscosity, Z-1 is more suitable for injection molding. Z-1 PVDF pellets as raw materials, the finished products has excell.. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527-1/-2 |
Unitika EX-1020K PA6, Conditioned Conducting nylonInformation provided by Unitika Ltd. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | |
Goodfellow Polyhydroxybutyrate - Biopolymer PHB PHB and its copolymers with polyhydroxyvalerate (PHV) are melt-processable semi-crystalline thermoplastics made by biological fermentation from renewable carbohydrate feedstocks. They have been desc.. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM D638 |
UBE UMERIT 1520F Metallocene LLDPE Description: UBE Super Polyethylene Umerit® is an ethylene-olefin copolymer made by UBE using the metallocene catalytic method. The metallocene catalytic method results in superior physical propert.. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527-1/-2 |
DSM Akulon® K225-KWS (Cond.) Nylon 6 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® BS EC PA6 Product description: Grilon BS 23 is an unreinforced, low viscosity and fine crystalline PA 6 injection molding grade. Grilon BS 23 has the following important properties: Good flow behaviorEasy pro.. |
|||
Tensile Strength, Yield | 40.0 MPa @Temperature 160 °C |
5800 psi @Temperature 320 °F |
ISO 527-1/-2 |
DSM Stanyl® TS300 PA46 |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® L 20 nat PA12 Medium viscosity unmodified Polyamide 12Information provided by EMS Grivory |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® TSZ 3 PA666 Product description: Grilon TSZ 3 is a heat stabilized, normal viscosity, high impact modified PA66 + PA6 injection molding grade. Grilon TSZ 3 has the following important properties: Excellent toug.. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® TSZ 3 PA666 Product description: Grilon TSZ 3 is a heat stabilized, normal viscosity, high impact modified PA66 + PA6 injection molding grade. Grilon TSZ 3 has the following important properties: Excellent toug.. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 |
Chi Mei Polylac® PA-709 ABS Super impact |
|||
Tensile Strength, Yield | 40.0 MPa @Temperature 80.0 °C |
5800 psi @Temperature 176 °F |
ASTM Test |
BASF Ultramid® 8202C PA6 (Dry) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | Conditioned 15 days at 23°C - 50% RH; ISO 527 |
Arkema Group Rilsan® PA 11 BESNO MED Nylon 11 Rilsan® PA 11 BESNO MED is a polyamide produced from a renewable source. This grade dedicated to extrusion offers the highest quality and it is specially designed to meet the stringent requirements.. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® A3Z BK 30464 PA66 (Conditioned) Description: Impact-modified and stabilized injection- molding grade for components and housings with good low temperature impact resistance.Information provided by BASF |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ASTM D638 |
Amco PRIMATOP PP HOMO 120NA-HF Multi-Purpose Polypropylene Features:medium viscosityexcellent processabilitygood stiffnessnucleationanti-statApplications:closuresthin wall applicationshousewaresFormer A-Top Polymers product; part of Amco product line since .. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® TS V0 X PA666 FR Product description: Grilon XE 5030 is a heat stabilized, flame retardant and self-extinguishing injection molding grade on the basis of PA6-PA66-alloy. Grilon XE 5030 features the following main pr.. |
|||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL EM6100 PPE+PS (Asia Pacific) Medium heat, high impact PPO/HIPS alloy used in the automotive industry. |