SABIC Innovative Plastics Xenoy® CL100 PBT+PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® CL100 PBT+PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Xenoy CL100 is an unfilled, impact modified, UV-stabilized PC/PBT blend with excellent solvent resistance and good low-temperature ductility. It has a proven track record in unpainted exterior automotive applications. ISO1043: PC+PBT-I.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm @Thickness 3.20 mm |
0.0070 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 14 g/10 min @Load 5.00 kg, Temperature 250 °C |
14 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Melt Index of Compound | 13 g/10 min @Load 5.00 kg, Temperature 250 °C |
13 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 96.0 MPa | 13900 psi | ISO 2039-1 |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 50 % | 50 % | Type I, 50 mm/min; ASTM D638 |
| 50 % | 50 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.15 GPa | 312 ksi | 1 mm/min; ISO 527 |
| 2.20 GPa | 319 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
| 85.0 MPa | 12300 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.05 GPa | 297 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.05 GPa | 297 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 7.00 J/cm | 13.1 ft-lb/in | ASTM D256 |
| 1.60 J/cm @Temperature -40.0 °C |
3.00 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| 1.70 J/cm @Temperature -30.0 °C |
3.18 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 6.00 J/cm @Temperature 0.000 °C |
11.2 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| 20.0 kJ/m² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 45.0 kJ/m² @Temperature 0.000 °C |
21.4 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 5.50 J/cm² | 26.2 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 50.0 J @Temperature 23.0 °C |
36.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 30 | 30 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 90.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 90.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Thermal Conductivity | 0.180 W/m-K | 1.25 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 90.0 °C | 194 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | |
| 90.0 °C @Thickness 3.20 mm |
194 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 125 °C | 257 °F | Rate B/50; ASTM D1525 |
| 125 °C | 257 °F | Rate B/50; ISO 306 | |
| 127 °C | 261 °F | Rate B/120; ISO 306 | |
| 160 °C | 320 °F | Rate A/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.3 @Frequency 50.0 - 60.0 Hz |
3.3 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 18.0 kV/mm @Thickness 1.00 mm |
457 kV/in @Thickness 0.0394 in |
short time; IEC 60243-1 | |
| Dissipation Factor | 0.0020 @Frequency 50.0 - 60.0 Hz |
0.0020 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- Mykroy/Mycalex MM 501 Molding Grade Glass-bonded Mica Composite
- Polykemi AB POLYblend 45H PC/ABS-blend, Flame Retardant
- Nihon Superior 95A Sn-Sb Lead-Free Solder Alloy
- SMAC CABLE® 2514S-30-10 Damping Material
- Diamond Polymers ABS 9500P Injection Molding Grade, Ultra High Impact Powder
- PolyOne Geon™ Vinyl Rigid Molding M4910 (USP CLASS VI for TRANS 9494 only) Polyvinyl Chloride, Rigid (PVC, Rigid)
- Zhejiang Juner PC-A1-9 Top-Grade Flame Retardant UV-Resistant
- A. Schulman POLYBLAK™ 4642 Premium Black Color Concentrate, 40% Carbon Black Based In LLDPE
- Overview of materials for Ionomer, Film Grade
- Overview of materials for Ethylene-Methyl Acrylate Copolymer, Molding Grade
Copyright © lookpolymers.com All Rights Reserved