SABIC Innovative Plastics NORYL EM6101 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL EM6101 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive interiors. Improved flow characteristics/overall processing economy. 250F DTUL. Good property retention/wide temperature range.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 50 % | 50 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 81.0 MPa | 11700 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 3.20 J/cm | 5.99 ft-lb/in | ASTM D256 |
| 1.60 J/cm @Temperature -40.0 °C |
3.00 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 53.0 J | 39.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 25.0 J @Temperature -30.0 °C |
18.4 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 93.6 µm/m-°C @Temperature 0.000 - 100 °C |
52.0 µin/in-°F @Temperature 32.0 - 212 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C @Thickness 6.40 mm |
250 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Q75B Polyurethane Rubber
- Parker Chomerics CHO-BOND 1076, Part A Silicone
- SABIC Innovative Plastics Lexan® EXL1162T PC Copolymer (Asia Pacific)
- Reade Advanced Materials Strontium Sulfate Powder (Celestite) (SrSO4)
- Lehmann & Voss LUVOCOM® 20-0916 Polyphthalamide, with carbon fiber
- Lanxess Durethan® BKV 130 CS DUS008 600091 Nylon 6, 30% Glass Fiber
- SABIC Innovative Plastics LNP THERMOCOMP DF004ER PC
- Fainplast Compounds FR 86/2 Flexible PVC, Insulation
- Azoty Tarnow™ TARNOFORM 500 POM
- ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 10% cold work (ASTM XM-8; UNS S43035)
Copyright © lookpolymers.com All Rights Reserved