SABIC Innovative Plastics Valox® 357X PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 357X PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
VALOX 357X is an impact modified, flame retarted PBT+PC blend. Applications like bobbins, switches and enclosures.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Viscosity | 310000 cP | 310000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.018 cm/cm | 0.011 - 0.018 in/in | on Tensile Bar; SABIC Method |
| 0.010 - 0.014 cm/cm @Thickness 3.20 mm |
0.010 - 0.014 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.018 cm/cm | 0.0090 - 0.018 in/in | on Tensile Bar; SABIC Method |
| Melt Flow | 9.6 g/10 min @Load 5.00 kg, Temperature 250 °C |
9.6 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| 13 g/10 min @Load 5.00 kg, Temperature 265 °C |
13 g/10 min @Load 11.0 lb, Temperature 509 °F |
ASTM D1238 | |
| 13 g/10 min @Load 5.00 kg, Temperature 266 °C |
13 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 | |
| Melt Index of Compound | 8.0 g/10 min @Load 5.00 kg, Temperature 250 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 10 g/10 min @Load 5.00 kg, Temperature 265 °C |
10 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ISO 2039-2 |
| Hardness, H358/30 | 115 MPa | 16700 psi | ISO 2039-1 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Type I, 50 mm/min; ASTM D638 |
| 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
| 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 30 % | 30 % | Type I, 50 mm/min; ASTM D638 |
| 30 % | 30 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.00 GPa | 290 ksi | 50 mm/min; ASTM D638 |
| 2.20 GPa | 319 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 78.0 MPa | 11300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| 2.10 GPa | 305 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 5.00 J/cm | 9.37 ft-lb/in | ASTM D256 |
| 1.50 J/cm @Temperature -30.0 °C |
2.81 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 1.90 J/cm @Temperature 0.000 °C |
3.56 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1A |
| 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 20.0 kJ/m² @Temperature 0.000 °C |
9.52 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | ISO 179/2C |
| NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/2C | |
| Charpy Impact, Notched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/2C |
| 4.50 J/cm² | 21.4 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Dart Drop, Total Energy | 35.0 J @Temperature 23.0 °C |
25.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 33 | 33 | CS-17, 1 kg; SABIC Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 3.0 @Frequency 50.0 - 60.0 Hz |
3.0 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| 17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | |
| 25.0 kV/mm @Thickness 1.60 mm |
635 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| 25.0 kV/mm @Thickness 1.60 mm |
635 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 34.0 kV/mm @Thickness 0.800 mm |
864 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0013 @Frequency 1.00e+6 Hz |
0.0013 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.0020 @Frequency 50.0 - 60.0 Hz |
0.0020 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| 0.013 @Frequency 1.00e+6 Hz |
0.013 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | >= 100 V | >= 100 V | IEC 60112 |
| 175 - 250 V | 175 - 250 V | UL 746A | |
| 225 V | 225 V | IEC 60112 | |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPC T4030 E20 Polypropylene Copolymer, Mineral Reinforced, Elastomer Modified
- LG Chemical LC565 Polyolefin Elastomer for Polymer Modification
- Techmer ES Electrafil® PP-61/EC Copolymer Polypropylene, Conductive Carbon Filled
- Solvay Specialty Polymers Polymist® XPP 552 Polytetrafluoroethylene (PTFE)
- Saint-Gobain COHRlastic® 1032 General-Purpose Electrical-Grade Silicone Coated Fabric
- Sumitomo Bakelite North America 775 CAF Mineral Filled Diallyl Phthalate
- Sylvin Technologies 5042N PVC Wire/Cable Compound
- China Tungsten ZP10-1 Tungsten Carbide
- Arkema Group Rilsan® AZM 15 TLD Nylon 12, 15% Glass Fiber Filled (Dry)
Copyright © lookpolymers.com All Rights Reserved