SABIC Innovative Plastics ULTEM ATX200R PEI Blend (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM ATX200R PEI Blend (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High flow Polyetherimide blend with internal mold release. RoHS compliant. UL94 V0 Listing.
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D792
Density 1.26 g/cc
0.0455 lb/in³
ISO 1183
Moisture Absorption 0.500 %
0.500 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.90 %
0.90 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on Tensile Bar; SABIC Method
0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 24 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 24 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D1238
Melt Index of Compound 16 g/10 min

@Load 5.00 kg,
Temperature 340 °C
 16 g/10 min

@Load 11.0 lb,
Temperature 644 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 125 MPa
18100 psi
ISO 2039-1
Tensile Strength at Break 75.0 MPa
10900 psi
50 mm/min; ISO 527
85.0 MPa
12300 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 95.0 MPa
13800 psi
50 mm/min; ISO 527
97.0 MPa
14100 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 20 %
20 %
50 mm/min; ISO 527
70 %
70 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 6.5 %
6.5 %
50 mm/min; ISO 527
7.0 %
7.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.00 GPa
435 ksi
1 mm/min; ISO 527
3.30 GPa
479 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 125 MPa
18100 psi
2 mm/min; ISO 178
145 MPa
21000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.10 GPa
450 ksi
2 mm/min; ISO 178
3.17 GPa
460 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
0.550 J/cm

@Temperature -30.0 °C
 1.03 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
26.7 J/cm

@Thickness 3.20 mm
 50.0 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Izod Impact, Unnotched 20.83 J/cm
39.02 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 50.0 J

@Temperature 23.0 °C
 36.9 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Taber Abrasion, mg/1000 Cycles 20
20
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature -40.0 - 150 °C
 27.8 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
50.0 µm/m-°C

@Temperature 23.0 - 150 °C
 27.8 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature -40.0 - 150 °C
 27.8 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
50.0 µm/m-°C

@Temperature 23.0 - 150 °C
 27.8 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
Thermal Conductivity 0.230 W/m-K
1.60 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 195 °C
383 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 180 °C
356 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
187 °C

@Thickness 3.20 mm
 369 °F

@Thickness 0.126 in
 unannealed; ASTM D648
191 °C

@Thickness 6.40 mm
 376 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 200 °C
392 °F
Rate B/50; ISO 306
205 °C
401 °F
Rate B/120; ISO 306
209 °C
408 °F
Rate B/50; ASTM D1525
210 °C
410 °F
Rate A/50; ISO 306
Flammability, UL94 V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
 UL 94
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
 2.9

@Frequency 1.00e+6 Hz
 IEC 60250
2.9

@Frequency 50.0 - 60.0 Hz
 2.9

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dissipation Factor 0.0010

@Frequency 50.0 - 60.0 Hz
 0.0010

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.0050

@Frequency 1.00e+6 Hz
 0.0050

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 150 V
150 V
IEC 60112
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2