Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Noryl
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics NORYL N190X PPE+PS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0/5VA rated. RTI Elec/Imp/Str 95/80/95. Dielectric strength. Suitable for E/E market applications.

Physical Properties	Metric	English	Comments
Specific Gravity	1.13 g/cc	1.13 g/cc	ASTM D792
Water Absorption	0.080 % @Time 86400 sec	0.080 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	20 g/10 min @Load 5.00 kg, Temperature 280 Â°C	20 g/10 min @Load 11.0 lb, Temperature 536 Â°F	ASTM D1238
Melt Index of Compound	23 g/10 min @Load 5.00 kg, Temperature 280 Â°C	23 g/10 min @Load 11.0 lb, Temperature 536 Â°F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM D785
Tensile Strength at Break	47.0 MPa	6820 psi	Type I, 50 mm/min; ASTM D638
	50.0 MPa	7250 psi	50 mm/min; ISO 527
Tensile Strength, Yield	58.0 MPa	8410 psi	50 mm/min; ISO 527
	60.0 MPa	8700 psi	Type I, 50 mm/min; ASTM D638
Elongation at Break	9.0 %	9.0 %	Type I, 50 mm/min; ASTM D638
	9.2 %	9.2 %	50 mm/min; ISO 527
Elongation at Yield	3.2 %	3.2 %	50 mm/min; ISO 527
	3.6 %	3.6 %	Type I, 50 mm/min; ASTM D638
Tensile Modulus	2.58 GPa	374 ksi	50 mm/min; ASTM D638
	2.60 GPa	377 ksi	1 mm/min; ISO 527
Flexural Yield Strength	87.0 MPa	12600 psi	2 mm/min; ISO 178
	91.0 MPa	13200 psi	2.6 mm/min, 100 mm span; ASTM D790
	98.0 MPa	14200 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	2.30 GPa	334 ksi	2.6 mm/min, 100 mm span; ASTM D790
	2.35 GPa	341 ksi	2 mm/min; ISO 178
	2.50 GPa	363 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	2.93 J/cm	5.49 ft-lb/in	ASTM D256
	1.00 J/cm @Temperature -30.0 Â°C	1.87 ft-lb/in @Temperature -22.0 Â°F	ASTM D256
Izod Impact, Unnotched	7.20 J/cm	13.5 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	20.0 kJ/mÂ²	9.52 ft-lb/inÂ²	80104; ISO 180/1A
Charpy Impact, Notched	2.00 J/cmÂ²	9.52 ft-lb/inÂ²	ISO 179/2C
Dart Drop, Total Energy	50.0 J @Temperature 23.0 Â°C	36.9 ft-lb @Temperature 73.4 Â°F	ASTM D3763
Taber Abrasion, mg/1000 Cycles	76	76	CS-17, 1 kg; ASTM D1044

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	77.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	42.8 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
CTE, linear, Transverse to Flow	81.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	45.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
Thermal Conductivity	0.240 W/m-K	1.67 BTU-in/hr-ftÂ²-Â°F	ASTM C177
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C	203 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	95.0 Â°C @Thickness 3.20 mm	203 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	82.0 Â°C	180 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	78.0 Â°C @Thickness 3.20 mm	172 Â°F @Thickness 0.126 in	unannealed; ASTM D648
	86.0 Â°C @Thickness 6.40 mm	187 Â°F @Thickness 0.252 in	unannealed; ASTM D648
Vicat Softening Point	104 Â°C	219 Â°F	Rate B/50; ASTM D1525
	107 Â°C	225 Â°F	Rate B/120; ISO 306
UL RTI, Electrical	95.0 Â°C	203 Â°F	UL 746B
UL RTI, Mechanical with Impact	80.0 Â°C	176 Â°F	UL 746B
UL RTI, Mechanical without Impact	95.0 Â°C	203 Â°F	UL 746B
Flammability, UL94	HB @Thickness 1.01 mm	HB @Thickness 0.0398 in	UL 94
	V-0 @Thickness 1.47 mm	V-0 @Thickness 0.0579 in	UL 94
	5VA @Thickness 2.99 mm	5VA @Thickness 0.118 in	UL 94
Oxygen Index	39 %	39 %	ASTM D2863

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.80e+16 ohm-cm	1.80e+16 ohm-cm	ASTM D257
Dielectric Constant	2.6 @Frequency 100000 Hz	2.6 @Frequency 100000 Hz	ASTM D150
	2.74 @Frequency 100 Hz	2.74 @Frequency 100 Hz	ASTM D150
Dielectric Strength	19.2 kV/mm @Thickness 3.20 mm	488 kV/in @Thickness 0.126 in	in oil; ASTM D149
Dissipation Factor	0.0055 @Frequency 100000 Hz	0.0055 @Frequency 100000 Hz	ASTM D150
	0.013 @Frequency 100 Hz	0.013 @Frequency 100 Hz	ASTM D150
Arc Resistance	0.00 - 60 sec	0.00 - 60 sec	Tungsten; ASTM D495
Comparative Tracking Index	400 - 600 V	400 - 600 V	UL 746A
Hot Wire Ignition, HWI	30 - 60 sec	30 - 60 sec	UL 746A
High Amp Arc Ignition, HAI	30 - 60 arcs	30 - 60 arcs	UL 746A
High Voltage Arc-Tracking Rate, HVTR	>= 150 mm/min	>= 5.91 in/min	UL 746A

Descriptive Properties	Value	Comments
UV-light, water exposure/immersion	F1	UL 746C