- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 187 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 187 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ISO 75-2 |
| Polycasa PS QUINN PS sheets have good optical properties and a brilliant surface. The QUINN PS range contains sheets that are easy to fabricate, to vacuum form, and show a high light transmission (min 88% wavel.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycolac® S708C ABS (Europe-Africa-Middle East) Cycolac* S708C is an improved scratch resistant ABS product with high stiffness and heat, used for applications in appliances, telecom, business machines and TV industries.This data was supplied by .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycoloy® EFX830ME PC Flame retardant modified PC blend using non-brominated and non-chlorinated flame retardant systems, offering metallic / sparkle look with minimal flow line visibilityThis data was supplied by SABIC-.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | 120°C/h; ASTM D 648 |
| Polimeri Europa Edistir ICE S 800/N Polystyrene
(discontinued **) Very high environmental stress cracking resistant (VH ESCR) modified HIPS. ICE S 800/N exhibits high toughness and excellent chemical resistance to oils, fats and chemical agents and in particular t.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ASTM D648 |
| Ineos Nova Zyntar® F7120 Developmental Flame Retardant Polystyrene
(discontinued **) Features: High flow for thin wall partsGood balance of physical propertiesUL94 V-0 @ 1.5 mm for black color Good aesthetics for injection molding Applications:Large television cabinetsConsumer elect.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP CG006 PS (Europe-Africa-Middle East) LNP* Lubricomp* CG006 is a compound based on Polystyrene resin containing Graphite. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | |
| Eastman Tenite 358-10 Cellulose Acetate Propionate
(discontinued **) 10% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.1 °C | 187 °F | ASTM D648 |
| Global 120-PC-Natural Acrylonitrile Styrene, General Purpose Grade Description-transparent, natural, medium impact resistance, high hardness, high heat resistance, good chemical resistanceApplications-automotive, electrical parts, household goodsInformation provide.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.1 °C | 187 °F | ASTM D648 |
| Global 121-PC-Blue Acrylonitrile Styrene, General Purpose Grade Description-transparent, blue, medium impact resistance, high hardness, good stiffness, high heat resistance, good chemical resistanceApplications-automotive, electrical parts, household goodsInform.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical RS656H ABS, Chemical Resistance to Cyclopentane Feature: Extrusion Molding, General Purpose, Chemical Resistance to CyclopentaneApplication: Refrigerator Inner LinerCAS No. 9003-56-9Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | injection molded unannealed; ASTM D-648-95 |
| Multibase Multi-ABS 802 Natural Extrusion Grade Data provided by Multibase. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-LOY A3000T ABS (Asia Pacific) LNP* Stat-loy* A3000T is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.1 °C | 187 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® ABS 8004 FR Availability: North AmericaForms: PelletsFeatures: Flame RetardantProcessing Method: ExtrusionInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® PT-0180 ABS, Unreinforced Painting Grade Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ISO 75 |
| Styrolution PS 168N GPPS Styrolution PS 168N is a high molecular weight, heat resistant grade used where high strength is required. Suitable for physically or chemically expanded extruded sheet. Also use as a blend componen.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® WR-9100SG ASA, Unreinforced Used for solid vinyl door, frame etc.Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.1 °C | 187 °F | Unannealed; 0.250 inches; ASTM D648 |
| TPI Porene® AS 121 PC (Blue) General Purpose SAN Porene® is a registered trademark of Thai Petrochemical Industry Co. LTD. Information provided by Dayson Polymers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | unannealed; ISO 75 |
| Chi Mei Kibilac® PW-997S ASA Polymer Extrusion |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | unannealed; ISO 75 |
| Chi Mei Polylac® PA-709S ABS - Extrusion Super Impact Extrusion |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ASTM D648, ISO 75 |
| EPICHEM Epilac ABS Acrylonitrile Butadiene Styrene |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | unannealed; ISO 75 |
| Chi Mei Polylac® PA-746H ABS - High Flow Super high flow, medium impact |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.1 °C | 187 °F | |
| Aclo Accutech ABS ABS832G10L Glass Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | |
| BASF Polystyrol® 168 N Polystyrene (Europe) High molecular, heat-resistant grades used where high strength is required. Suitable for expanded film.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ISO 75 |
| BASF Ultramid® 1310-11 NF2001 PA66 (Dry) Ultramid 1310-11 NF2001 is a controlled crystallization, fast cycling PA6/6 which provides extremely fast cycle times and improved productivity over Ultramid 1000. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP PH0320A PA 6 LNP THERMOCOMP* PH0320A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | 0.5 inch; ASTM D648 |
| PlastxWorld DAICEL STYROL® SK50H HIPS Flame retarded HIPSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ASTM D648 |
| Samyang Trimma® SD6350T PMMA, Opaque High scratch resistance; stability against weak acids, strong acids, weak alkalis and inorganic salts.Information provided by Samyang. |
|||