Stellarchem SV-B70E TPV Compound
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV) |
| Manufacturer | Stellarchem |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Stellarchem SV-B70E TPV Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This grade of Stellarchem SV series is a dynamic crosslinked, EPDM/PP compound. It's design to replace thermoset elastomers, such as EPDM, and traditional Thermoplastic TPVs. It can be process on conventional thermoplastics equipment for injection molding or extrusion, provides the performance of vulcanized rubber with the advantage of low cost thermoplastic processing. It's a soft, EPDM/PP based, completely recyclable & colorable elastomer material. It's formulated to overmold to PP thermoplastics in normal dual injection & extrusion processing.Information provided by Stellarchem Polymer & Industrial
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D792 |
| Particle Mesh Size | 80 - 150 Mesh | 80 - 150 Mesh | |
| Melt Flow | 21 g/10 min @Load 10.0 kg, Temperature 230 °C |
21 g/10 min @Load 22.0 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | ASTM D2240 |
| Tensile Strength, Ultimate | 7.35 MPa | 1070 psi | ASTM D412 |
| Elongation at Break | 450 % | 450 % | ASTM D412 |
| 100% Modulus | 0.02842 GPa | 4.122 ksi | ASTM D412 |
| Tear Strength | 29.4 kN/m | 168 pli | ASTM D412 |
| Compression Set | 33 % @Temperature 70.0 °C, Time 79200 sec |
33 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 160 - 170 °C | 320 - 338 °F | Metering Temperature, Extrusion |
| Rear Barrel Temperature | 150 - 160 °C | 302 - 320 °F | Extrusion |
| 160 - 190 °C | 320 - 374 °F | Injection Molding | |
| Middle Barrel Temperature | 155 - 165 °C | 311 - 329 °F | Transition, Extrusion |
| 170 - 190 °C | 338 - 374 °F | Injection Molding | |
| Front Barrel Temperature | 170 - 180 °C | 338 - 356 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection Molding | |
| Nozzle Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Die Temperature | 170 - 180 °C | 338 - 356 °F | Extrusion |
| Melt Temperature | 150 - 180 °C | 302 - 356 °F | Extrusion |
| 160 - 200 °C | 320 - 392 °F | Injection Molding | |
| Mold Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Injection Molding |
| Injection Pressure | 5.00 - 40.0 MPa | 725 - 5800 psi | Injection Molding |
| Back Pressure | 0.500 - 1.00 MPa | 72.5 - 145 psi | Injection Molding |
| Screw Speed | 60 - 100 rpm | 60 - 100 rpm | Extrusion |
| 100 - 200 rpm | 100 - 200 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Polimeri Europa Extir® B 2000 Expandable Polystyrene, Fast Molding (discontinued **)
- Henkel Turco 5884 Jet Engine Cleaner, Compressor Wash
- Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GMAW spray weld 1.1 mm diameter filler wire
- UBE UBEPOL VCR303 Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- Dalau Dalcon 001 100% Virgin PTFE
- Fainplast Compounds HAX HFX 024-15C Halogen Free PVC
- BASF Lupranate® 275 Isocyanate
- Phillips 66 COPYLENE® CR300CL-01 Polypropylene Random Copolymer
- DuPont Performance Polymers Zytel® HTN 52G35EF BK420 Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved