SABIC Innovative Plastics Lexan® FXD941A PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® FXD941A PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent/translucent PC for light diffusion special effects. Color package may affect performance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10.2 g/10 min @Load 1.20 kg, Temperature 300 °C |
10.2 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 71.0 MPa | 10300 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 130 % | 130 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.26 GPa | 328 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.39 GPa | 347 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 75.0 J @Temperature 23.0 °C |
55.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | V-2 @Thickness 1.52 mm |
V-2 @Thickness 0.0598 in |
UL 94 |
| V-0 @Thickness 3.04 mm |
V-0 @Thickness 0.120 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 80 % | 80 % | transparent/translucent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V75N Fluoroelastomer Compound
- DuPont Performance Polymers Crastin® S650FR BK851 PBT (Unverified Data**)
- NOVA Chemicals Sclair® 8306 UV8D, 8306G UV8D MDPE Rotational Molding Resin (discontinued **)
- Silberline Silvex® 333-20-C
- Master Bond EP21TDC-4 Two Component, Highly Flexible Epoxy System
- Lubrizol Estane® ALR CL65D Thermoplastic Polyurethane
- Colorite Polymers 6511 Clear Extrusion Vinyl Compound
- 3M Dyneon™ Dynamar™ FX 5920B Polymer Processing Additive
- Bulk Molding Compounds BMC 1423 Wear Resistant, Electrical Grade
- BASF Ultradur® B 4300 G6 LT 30% Glass Filled BK 150926 PBT
Copyright © lookpolymers.com All Rights Reserved