Total PPH 3271 Polypropylene, Oriented Film Extrusion Grade
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Total Atofina |
| Trade Name | PPH |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Total PPH 3271 Polypropylene, Oriented Film Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Homopolymer film gradeLow Residuals – FINA 3271 utilizes the new Fina proprietary process technology to provide extremely low residuals for improved color stability and clarity.Slip/Antiblock – FINA 3271 is available with custom slip and antiblock packages.FDA – FINA 3271 complies with all application FDA regulations for food contact applications.Recommended Applications -- FINA 3271 is recommended in orientation processes for manufacture of packaging tapes and films.Processing – FINA 3271 resin processes on oriented film extrusion equipment with typical melt temperatures of 450°F-525°F (232°C-274°C)Data provided by the manufacturer, Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ASTM D1505 |
| Water Vapor Transmission | 4.70 g/m²/day @Temperature 37.8 °C |
0.303 g/100 in²/day @Temperature 100 °F |
90% RH; thickness not specified; ASTM E96 |
| Melt Flow | 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 150 % | 150 % | ASTM D882 |
| Film Elongation at Break, TD | 50 % | 50 % | ASTM D882 |
| Secant Modulus, MD | 2.41 GPa | 350 ksi | ASTM D882 |
| Secant Modulus, TD | 4.14 GPa | 600 ksi | ASTM D882 |
| Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 163 °C | 325 °F | DSC |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Gloss | 85 % | 85 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 274 °C | 450 - 525 °F | oriented film extrusion |
Users viewing this material also viewed the following:
- Rogers Corporation Bisco™ BF-1000 Cellular Silicone Foam
- Total Finaprene® 602 Styrene-Butadiene TPE Copolymer Compound, Formulated to 61 Shore A (discontinued **)
- Nilit FRIANYL B63 SG 10 Nylon 6 for injection molding, 10% mineral filled
- SABIC Innovative Plastics LNP THERMOCOMP PF006S PA 6 (Europe-Africa-Middle East)
- Techmer ES HiFill FR® HDPE FR-2
- Hexcel® HexForce™ 1527 Fiber Glass Fabric
- A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6
- Eurostar Starflam RF0069 PA66, 30% Glass Fiber, Flame Retardant, Injection Molded
- Bhansali Engineering Abstron HR-105 ABS Super Heat Resistant
- SABIC Innovative Plastics PREVEX W20 PPE+PS
Copyright © lookpolymers.com All Rights Reserved