SABIC Innovative Plastics LNP KONDUIT PX08321 PA 6 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Konduit
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP KONDUIT PX08321 PA 6 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Thermally conductive mineral filled PA6 compound
Physical Properties Metric English Comments
Density 1.61 g/cc
0.0582 lb/in³
ASTM D792
Water Absorption 0.34 %

@Time 86400 sec
 0.34 %

@Time 24.0 hour
 SABIC Method
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0046 cm/cm

@Time 86400 sec
 0.0046 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0039 cm/cm

@Time 86400 sec
 0.0039 in/in

@Time 24.0 hour
 ASTM D955
Melt Flow 12.2 g/10 min

@Load 6.70 kg,
Temperature 285 °C
 12.2 g/10 min

@Load 14.8 lb,
Temperature 545 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa
10200 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 0.90 %
0.90 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 13.82 GPa
2004 ksi
50 mm/min; ASTM D638
Flexural Strength 104 MPa
15100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 14.2 GPa
2060 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.240 J/cm
0.450 ft-lb/in
ASTM D256
Izod Impact, Unnotched 1.57 J/cm
2.94 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 16.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
 9.06 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
36.3 µm/m-°C

@Temperature 40.0 - 120 °C
 20.2 µin/in-°F

@Temperature 104 - 248 °F
 ASTM E 831
CTE, linear, Transverse to Flow 28.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 15.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
55.6 µm/m-°C

@Temperature 40.0 - 120 °C
 30.9 µin/in-°F

@Temperature 104 - 248 °F
 ASTM E 831
Thermal Conductivity 1.10 W/m-K
7.63 BTU-in/hr-ft²-°F
through-plane, ø80*3mm discs; ISO 22007-2
2.60 W/m-K
18.0 BTU-in/hr-ft²-°F
through-plane, 10*10*3mm sample; ASTM E 1461-07
8.57 W/m-K
59.5 BTU-in/hr-ft²-°F
in-plane, ø80*3mm discs; ISO 22007-2
10.0 W/m-K
69.4 BTU-in/hr-ft²-°F
in-plane, ø25*0.4mm disc; ASTM E 1461-07
Deflection Temperature at 1.8 MPa (264 psi) 192 °C

@Thickness 3.20 mm
 378 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 1.00 mm
 HB

@Thickness 0.0394 in
 UL 94
Glow Wire Test 825 °C
1520 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Dielectric Constant 4.1

@Frequency 1.00e+6 Hz
 4.1

@Frequency 1.00e+6 Hz
 ASTM D150
6.2

@Frequency 50.0 - 60.0 Hz
 6.2

@Frequency 50.0 - 60.0 Hz
 ASTM D150
Dielectric Strength 14.7 kV/mm

@Thickness 1.00 mm
 373 kV/in

@Thickness 0.0394 in
 in oil; ASTM D149
Dissipation Factor 0.044

@Frequency 1.00e+6 Hz
 0.044

@Frequency 1.00e+6 Hz
 ASTM D150
0.076

@Frequency 50.0 - 60.0 Hz
 0.076

@Frequency 50.0 - 60.0 Hz
 ASTM D150
Comparative Tracking Index 600 V
600 V
IEC 60112
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A