SABIC Innovative Plastics LNP THERMOCOMP AF003 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP AF003 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* AF003 is a compound based on ABS resin containing 15% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.240 % | 0.240 % | 50% RH, 24 hrs; ASTM D570 |
| 0.350 % | 0.350 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 69.0 MPa | 10000 psi | 5 mm/min; ISO 527 |
| 70.0 MPa | 10200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 | |
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 5.16 GPa | 748 ksi | 1 mm/min; ISO 527 |
| 5.35 GPa | 776 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 103 MPa | 14900 psi | ISO 178 |
| 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 112 MPa | 16200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.51 GPa | 654 ksi | 2 mm/min; ISO 178 |
| 4.90 GPa | 711 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.96 J/cm | 5.55 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 14.0 J @Temperature 23.0 °C |
10.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 68.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 103 °C @Thickness 3.20 mm |
217 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8110 (UF) Synthetic Oil
- PTS Tristar® PC-06 6 MFI Extrusion Grade Polycarbonate
- PolyChem Alloy 5006 Talc Nucleator
- Lehmann & Voss PLASLUBE NY-1/TF/20/BK Polyamide 66, with PTFE
- Lucite International Elvacite ® 2550 Acrylic Resin
- SABIC Innovative Plastics LNP THERMOCOMP UF008H PPA
- Hexcel® HexPly® 916 120°C Curing Epoxy Matrix
- Hexcel® HexWeb® CR III 1/4-5052-.0025 Corrosion Resistant Specification Grade Aluminum Honeycomb
Copyright © lookpolymers.com All Rights Reserved