- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 91.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 91.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycolac® EX39F ABS Highest impact extrusion ABS for sheet and blow molding applications. FDA food contact compliant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Cycolac® S701 ABS (Europe-Africa-Middle East) CYCOLAC S701 is a new developed ABS providing a superior balance of properties. Its wide processing window, excellent flow and good mechanical properties give this material an excellent fit in appli.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics GELOY CR7520 ASA General purpose ASA. Excellent weatherability, good flow/aesthetics and high impact. Rated F2 by UL. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS (Europe-Africa-Middle East) LNP* LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Ineos ABS Centrex® 833 ASA+AES Blend
(discontinued **) Key Features:UnfilledHigh impact or high impact modifiedLight stabilized or stable to lightU.V. stabilized or stable to weatherSuitable processing methods:Profile extrusionSheet extrusionThermoformi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Eastman Tenite 371A-12 CAP Cellulose Acetate Propionate
(discontinued **) 12% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ASTM D648 |
| LyondellBasell Pro-fax 6329 Polypropylene Homopolymer, Improved Chemical Resistance Key Features: improved chemical resistance polypropylene homopolymer resin, FDA acceptable, easier processingApplications: closures, housewares, chairsMeets FDA requirements in 21 CFR 177.1520 for a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ASTM D648 |
| Flint Hills P9H9Z-018 Polypropylene Specialty polypropylene, UL certified, and FDA compliant.Applications: Extrusion coating.Former Huntsman polypropylene products are now produced by Flint Hills Resources. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Inchem Phenoxy PKFE Phenoxy PKFE - polyhydroxy ether of Bisphenol A. Originally developed by Union Carbide. Produced by InChem Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 6.40 mm |
196 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical HIPS MI750L PS, Impact Modified Description: Injection Molding, PS, Impact Modified, High GlossApplication: Electric/Electronic Components, Stationary Articles, Food Containers, etc.CAS: 9003-55-8Information provided by LG Chemica.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 6.40 mm |
196 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical PI641 ABS, High Impact Feature: Extrusion Molding, General Purpose, High ImpactApplication: Pipe FittingCAS No. 9003-56-9Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ASTM D648 |
| Flint Hills P5M6N-058A Polypropylene Random Copolymer Features: Excellent processabilty, nucleated and antistat. Product does not contain animal derived components. Phthalate-free.Applications: Injection Molding: consumer disposable itemsInformation .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Ineos ABS Triax® 1120 ABS + Polyamide Blend (DAM) Key Features:UnfilledPlatableHigh impact or high impact modifiedSuitable processing methods:Injection moldingFilm extrusionBlow molding |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, Dry as Molded Injection molding grade with good flow and stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical damping be.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Ineos ABS TRIAX® 1220 S ABS/Nylon Blend, Dry as Molded Extrusion and injection molding grade with good stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical dampi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Ineos ABS Triax® KU 2-3050 ABS + Polyamide Blend (DAM) Key Features:UnfilledHigh impact or high impact modifiedLight stabilized or stable to lightHeat stabilized or stable to heatSuitable processing methods:Injection molding |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 6.40 mm |
196 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Prevex VFAX PPE+PS High impact strength. 180F (82C) HDT. Improved productivity/reliability.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON AX00756 ABS LNP STAT-KON* AX00756 is a compound based on ABS resin containing Stainless Steel. Added feature of this material is: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON DD0001I PC LNP* STAT-KON* DD0001I is a compound based on Polycarbonate resin containing Carbon Powder. Added features include: ECO FR rating of 94V-0 @ 3.0mm and 94V-1 @ 1.5mm, High Impact. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Stat-loy A3000Z ABS LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75 |
| Teijin Multilon TN-7500F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. High stiffness and flowability realize the thin wall of large-scale business machine chassis.Information provided by Tei.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ASTM Test |
| Styrolution Terluran® GP-22 ABS Terluran GP-22 is an easy flowing grade of ABS for injection molding with high resistance to impact and heat deflection.Information provided by STYROLUTION, which is a joint venture between BASF and.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75-2 |
| Borealis BC545MO Polypropylene Copolymer BC545MO is a low-blush polypropylene heterophasic copolymer intended for injection molding. This grade features high impact strength, high thermal stability and very good process ability. As all pol.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75-2 |
| Borealis HK030U Polypropylene Compound HK030U is a special low viscosity polypropylene compound developed to fit the production of PP-GF composites in the direct LFT compression and injection molding process as well as in combination wit.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Method A; ASTM D648 |
| Chevron Phillips Marlex® K605 HDPE Blow Molding Resin Resin Type: Ethylene HomopolymerCharacteristics: Good ESCRExceptional rigidityExcellent melt strengthApplications: Automotive bumper beamsInformation provided by Chevron Phillips. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75B |
| Dow INSPIRE™ 112 Performance Polymer INSPIRE™ 112 Performance Polymer is a propylene-based resin intended for use in film and sheet extrusion.Information provided by Dow |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 6.40 mm |
196 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical HIPS MI750 PS, Impact Modified Description: Injection Molding, PS, Impact Modified, High GlossApplication: Electric/Electronic Components, Stationary Articles, Food Containers, etc.CAS: 9003-55-8Information provided by LG Chemica.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75-2 |
| Borealis Daplen™ KSX65T20 Polypropylene Compound 20% Mineral Filled Daplen KSX65T20 is a 20% mineral filled grade intended for injection molding. Daplen KSX65T20 has been developed especially for the car industry, to be used in interior parts. Daplen KSX65T20 offe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Eastman Tenite 383A-12 CAP Cellulose Acetate Propionate
(discontinued **) 12% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 - 106 °C | 196 - 223 °F | Average value: 100 °C Grade Count:7 |
| Overview of materials for Acrylic, Optical Grade, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Optical Grade, Molded". Each property range of values reported is minimum and maximum values of.. |
|||