SABIC Innovative Plastics Cycoloy® CM6140 PC+ABS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CM6140 PC+ABS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cycoloy resin grade CM6140 is a flame retardant, filled PC/ABS blend. It is of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm. Key features include thin wall FR, higher stiffness, balanced properties in flow, impact and heat designed for various thin wall applications.
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D792
Density 1.25 g/cc
0.0452 lb/in³
ISO 1183
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ASTM D570
Moisture Absorption 0.0100 %
0.0100 %
50% RH, 24 hrs; ASTM D570
0.0100 %
0.0100 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.090 %
0.090 %
ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0050 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 17.5 g/10 min

@Load 2.16 kg,
Temperature 260 °C
17.5 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 14 g/10 min

@Load 5.00 kg,
Temperature 220 °C
14 g/10 min

@Load 11.0 lb,
Temperature 428 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
Type I, 5 mm/min; ASTM D638
50.0 MPa
7250 psi
5 mm/min; ISO 527
Tensile Strength, Yield 65.0 MPa
9430 psi
Type I, 50 mm/min; ASTM D638
65.0 MPa
9430 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 15 %
15 %
50 mm/min; ISO 527
100 %
100 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 3.5 %
3.5 %
5 mm/min; ISO 527
4.0 %
4.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.20 GPa
464 ksi
1 mm/min; ISO 527
3.50 GPa
508 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 97.0 MPa
14100 psi
2 mm/min; ISO 178
100 MPa
14500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.30 GPa
479 ksi
1.3 mm/min, 50 mm span; ASTM D790
3.45 GPa
500 ksi
2 mm/min; ISO 178
Izod Impact, Notched 2.00 J/cm
3.75 ft-lb/in
ASTM D256
0.880 J/cm

@Temperature -30.0 °C
1.65 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*3; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 50.0 J

@Temperature 23.0 °C
36.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 97.0 °C

@Thickness 6.40 mm
207 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
83.0 °C

@Thickness 3.20 mm
181 °F

@Thickness 0.126 in
unannealed; ASTM D648
89.0 °C

@Thickness 6.40 mm
192 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 91.0 °C
196 °F
Rate B/50; ASTM D1525
98.0 °C
208 °F
Rate B/50; ISO 306
102 °C
216 °F
Rate B/120; ISO 306
Flammability, UL94 V-1

@Thickness 0.600 mm
V-1

@Thickness 0.0236 in
UL 94
V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
UL 94
5VB

@Thickness 1.50 mm
5VB

@Thickness 0.0591 in
UL 94
Glow Wire Test 800 °C
1470 °F
IEC 60695-2-13
850 °C
1560 °F
IEC 60695-2-13
960 °C

@Thickness 0.800 mm
1760 °F

@Thickness 0.0315 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 2.68e+16 ohm-cm
2.68e+16 ohm-cm
ASTM D257
Surface Resistance 3.54e+15 ohm
3.54e+15 ohm
ASTM D257
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASSES
IEC 60695-10-2