Styron Pulse® 979 PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® 979 PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PULSEâ„¢ 979 is a high performance, 10% glass filled PC/ABS resin.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | DIN 53752 |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 260 °C |
12 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 10 mm/min; ISO 3268 |
| Tensile Modulus | 4.00 GPa | 580 ksi | 1 mm/min; ISO 3268 |
| Flexural Strength | 120 MPa | 17400 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 3.70 GPa | 537 ksi | 3 points and 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/4A |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179 |
| 3.00 J/cm² @Temperature -40.0 °C |
14.3 ft-lb/in² @Temperature -40.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -40.0 °C |
2.38 ft-lb/in² @Temperature -40.0 °F |
ISO 179 |
| 0.650 J/cm² @Temperature -20.0 °C |
3.09 ft-lb/in² @Temperature -4.00 °F |
ISO 179 | |
| 0.700 J/cm² @Temperature 0.000 °C |
3.33 ft-lb/in² @Temperature 32.0 °F |
ISO 179 | |
| 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C @Temperature 0.000 - 80.0 °C |
27.8 µin/in-°F @Temperature 32.0 - 176 °F |
ASTM D696 |
| Vicat Softening Point | 131 °C | 268 °F | 50N / 50°C/hr; ISO 306B |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F |
Users viewing this material also viewed the following:
- Lucas-Milhaupt EASY FLO Silver Based Cadmium-Bearing Filler Metal
- SABIC Innovative Plastics ULTEM CRS5301 PEI
- Teknor Apex Laripur® LPR 9060HFM Thermoplastic Polyurethane
- PlastxWorld CEVIAN®-N 055 SAN resin
- Covestro Apec® HT KU 1-9354 High-Heat Polycarbonate
- A. Schulman POLYBLAK™ 4642 Premium Black Color Concentrate, 40% Carbon Black Based In LLDPE
- Axiall 3240 Rigid PVC, Extrusion
- DuPont Bynel® 41E558 Anhydride-Modified LLDPE Adhesive Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved