A. Schulman POLYFLAM™ FPP 1006 Talc Filled Homopolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFLAM™ FPP 1006 Talc Filled Homopolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® FPP 1006 is a 20% talc filled homopolymer polypropylene compound.Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Modulus | 2.275 GPa | 330.0 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | ASTM D648 |
| UL RTI, Electrical | 65.0 °C @Thickness 0.780 mm |
149 °F @Thickness 0.0307 in |
UL 746 |
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.780 mm |
149 °F @Thickness 0.0307 in |
UL 746 |
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.780 mm |
149 °F @Thickness 0.0307 in |
UL 746 |
| Flammability, UL94 | HB @Thickness 0.780 mm |
HB @Thickness 0.0307 in |
Users viewing this material also viewed the following:
- Nye Lubricants 571H-2 (NT) Synthetic Oil
- SABIC Innovative Plastics Lexan® HF500R PC (Europe-Africa-Middle East)
- Mid-Mountain Materials HYTEX® 2200 Ceramic Fiber Industrial Textile
- SABIC Innovative Plastics LNP THERMOCOMP WX05502 Polyester Elastomer
- Total PS CPDS 853 Flame Retardant Polystyrene
- Daikin POLYFLON MG-1040 PTFE 20% Glass Fiber Filled Molding Powder
- Eurotec® Tecodur® PB70 GR15 BK002 WX21 PBT, 15% glass fiber reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural
- Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (2 mm Molded Thickness)
- Chang Chun Plastic Longlite PM T373J Electrical Phenolic Molding Compound
- Formosa Plastics Formolene® 5181K Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved