SABIC Innovative Plastics Cycolac® MG29 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® MG29 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Super high impact ABS. Good low temperature toughness. High gloss.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Viscosity | 280000 cP | 280000 cP | Melt Viscosity, 240°C, 1000 sec-1; ASTM D3825 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 1.2 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.2 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| 10 g/10 min @Load 10.0 kg, Temperature 220 °C |
10 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 31.0 MPa | 4500 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 26 % | 26 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 1.99 GPa | 289 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 64.0 MPa | 9280 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.06 GPa | 299 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 4.53 J/cm | 8.49 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 28.0 J @Temperature 23.0 °C |
20.7 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 93.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C @Thickness 3.20 mm |
205 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C @Thickness 3.20 mm |
178 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 98.0 °C | 208 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.52 mm |
HB @Thickness 0.0598 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | UL 746A |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min | 0.000 - 0.394 in/min | UL 746A |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 T 30 Polyamide 66, 30% Mineral Filled
- Premix Thermoplastics PRE-ELEC® ESD 7100
- Polymer Resources PC-GP4-[color]-6 Polycarbonate, FDA-compliant Feedstocks, Easy Flow with Mold Release
- Northstar Polymers PBA-055 Polyether Curing Agent
- Mueller Alloy 3600 Free Cutting Brass (UNS C36000)
- SABIC Innovative Plastics LNP STAT-KON Noryl_HMC3008A PPE+HIPS (Europe-Africa-Middle East)
- A. Schulman POLYAXIS® LPA815 LPA 815EVA
- Akzo Nobel Trigonox® C-50D-pd Peroxide Cure Agent
- Ametek Tungsten-Copper Composites AWC 8020
Copyright © lookpolymers.com All Rights Reserved