Oxford Polymers 30GF 30% Glass Fiber Filled Polycarbonate for Injection Molding
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled |
| Manufacturer | Oxford Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Oxford Polymers 30GF 30% Glass Fiber Filled Polycarbonate for Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Fiber Filled Polycarbonate for Injection MoldingInformation provided by Oxford Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 131 MPa | 19000 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 8.62 GPa | 1250 ksi | ASTM D638 |
| Flexural Strength | 159 MPa | 23000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Compressive Strength | 124 MPa | 18000 psi | ASTM D695 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 23.0 °C |
2.00 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 305 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 293 °C | 560 °F | |
| Back Pressure | 103 MPa | 15000 psi | Mold pressure |
Users viewing this material also viewed the following:
- RheTech Products T20P200-01BG 20% Talc Reinforced Polypropylene Copolymer, General Purpose Black, Blow Molding Grade
- SABIC PP 578P Polypropylene Homopolymer for Injection Molding
- PSM Industries Pacific Sintered Metals High Strength Nickel Steel FN-256-T(HT) Powdered Metal
- SABIC Innovative Plastics Lexan® FST9705 PC Copolymer
- SABIC Innovative Plastics Cycoloy® C6200 PC+ABS
- NextGen Adhesives G907-08 Epoxy Adhesive
- Indium Corp. Indalloy 141 Tin-Lead Solder Alloy
- Covestro Bayfill® 361 Polyurethane Semi-Rigid Foam, Conventional Catalyst, Open Pour, MDI-based 2-Component Liquid System
- Clariant Renol SB83642580 ASA Polymer
- 3M Scotchcal™ 50-100 Graphic Film
Copyright © lookpolymers.com All Rights Reserved