Dow ATTANE™ 4404G, 2mil Ultra Low Density Ethylene/Octene Copolymer

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Dow Chemical
Trade Name ATTANE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow ATTANE™ 4404G, 2mil Ultra Low Density Ethylene/Octene Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ATTANE™ 4201G provides improved cling in one-sided cling applications, and has improved toughness and optical properties. It complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a.Information provided by Dow
Physical Properties Metric English Comments
Density 0.904 g/cc
0.0327 lb/in³
ASTM D792
Water Vapor Transmission 16.7 g/m²/day
1.08 g/100 in²/day
1 atm, 38°C, 100% RH; ASTM D1249
Oxygen Transmission 445.7 cc-mm/m²-24hr-atm
1132 cc-mil/100 in²-24hr-atm
ASTM D3985
Carbon Dioxide Transmission 2022 cc-mm/m²-24hr-atm
5136 cc-mil/100 in²-24hr-atm
Dow Method
Thickness 50.8 microns
2.00 mil
Melt Flow 4.0 g/10 min
4.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 6.76 MPa
980 psi
ASTM D882
Film Tensile Strength at Yield, TD 6.34 MPa
919 psi
ASTM D882
Film Elongation at Break, MD 664 %
664 %
ASTM D882
Film Elongation at Break, TD 714 %
714 %
ASTM D882
Secant Modulus, MD 0.062563 GPa
9.0741 ksi
2% Secant; ASTM D882
Secant Modulus, TD 0.06298 GPa
9.135 ksi
2% Secant; ASTM D882
Impact 211
211
[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
Elmendorf Tear Strength MD 955 g
955 g
ASTM D1922
Elmendorf Tear Strength TD 1100 g
1100 g
ASTM D1922
Elmendorf Tear Strength, MD 18.80 g/micron
477.5 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 21.7 g/micron
550 g/mil
ASTM D1922
Dart Drop Test >= 850 g
>= 1.87 lb
Method B; ASTM D1709
Film Tensile Strength at Break, MD 32.60 MPa
4728 psi
ASTM D882
Film Tensile Strength at Break, TD 32.43 MPa
4703 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 124 °C
255 °F
Dow Method (DSC)
Vicat Softening Point 71.0 °C
160 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 1.8 %
1.8 %
ASTM D1003
Gloss 90 %
90 %
45°; ASTM D2457
Transmission, Visible 99 %
99 %
Clarity; ASTM D1746