Clariant Renol PBTSP0006 Polyester Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PBTSP0006 Polyester Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 8.89 MPa | 1290 psi | ASTM D638 |
| Elongation at Break | 430 % | 430 % | ASTM D638 |
| Flexural Modulus | 0.210 GPa | 30.5 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 221 - 238 °C | 430 - 460 °F | |
| Mold Temperature | 10.0 - 21.1 °C | 50.0 - 70.0 °F | |
| Dry Time | 2 - 4 hour @Temperature 104 °C |
2 - 4 hour @Temperature 220 °F |
to ensure moisture content is less than 0.02% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA-61 General Purpose Acrylic Resin
- Lanxess Durethan® BKV 15 H2.0 901510 Copolyamide, 15% Glass Fiber
- Karina 804D40/146-AT Green PVC Compound
- Heatbath/Park Cartecsal Neutral Salt
- Indium Corp. Germanium Corporation® Germanium Metal
- Schwartz Technical Plastics LAMIGAMID® 700 Ultra High Molecular Weight Polyethylene
- Techmer ES HiFill® PA6/6 GF33 SF L 33% Glass Filled
- Styron CALIBREâ„¢ 201-06 Polycarbonate
- Sumitomo Bakelite North America 51-01 CAFR-P Mineral Filled Diallyl Phthalate
- Asahi Kasei Tenac®-C MT754 Copolymer Acetal Resin
Copyright © lookpolymers.com All Rights Reserved