Polymer Property : Tensile Strength at Break = 4500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	31.0 MPa	4500 psi	2 in/min; ASTM D638
RheTech Products M20P100-01 20% Mica Reinforced Polypropylene, Black Applications: Fan shroudsFiller panelsAir ductsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	31.0 MPa	4500 psi	2 in/min; ASTM D638
RheTech Products T12P600-430UVBG 12% Talc Reinforced Polypropylene Copolymer, UV Stabilized, Interior 848 Black, Blow Molding Grade Applications: Flipper panelsSeat backsLoad floorInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	31.0 MPa	4500 psi	2 in/min; ASTM D638
RheTech Products T20P100-00 20% Talc Reinforced Polypropylene, Natural Applications: Electronic housingsConsolesIP componentsHVAC ducts - air distributionClose out panelDurable goodsInjection molding conditions reported in table.Information provided by RheTech Products..
Tensile Strength at Break	31.0 MPa	4500 psi	2 in/min; ASTM D638
RheTech Products T20P100-01UV 20% Talc Reinforced Polypropylene, UV Stabilized, General Purpose Black Applications: Durable goodsElectronics housingsIP componentsClose out panelsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	31.0 MPa	4500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Cycolac® MG34LG ABS Automotive: Low gloss ABS for unpainted interior applications.
Tensile Strength at Break	>= 31.0 MPa	>= 4500 psi	ASTM D638
Niche Polymer PPHM15BK Homopolymer PP Information provided by Niche Polymer
Tensile Strength at Break	31.0 MPa	4500 psi	2 in/min; ASTM D638
RheTech Products HP532-00 20% Talc Reinforced High Performance Polypropylene, Non-UV Stabilized, Natural Applications: Interior trimCenter tail light bezelPackage trayInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	31.0 MPa	4500 psi	ASTM D638
Eastman 9921P PET Injection Molded (discontinued **) Voridian PET 9921P is produced at Voridian’s manufacturing sites in Rotterdam and Zarate, it is PTA/CHDM based, and it is sold to customers in the Europe, Middle East and Africa, Argentina, Bolivia..
Tensile Strength at Break	31.0 MPa @Temperature 100 °C	4500 psi @Temperature 212 °F	ISO 527
Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **) AMODEL ET-1001 L resin is an impact modified polyphthalamide (PPA) with exceptional impact strength and practical toughness. AMODEL PPA resins offer high fatigue strength, and good chemical resistan..
Tensile Strength at Break	<= 31.0 MPa	<= 4500 psi	ISO/R527
Polykemi AB POLYfill PPH T1040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Tensile Strength at Break	31.0 MPa	4500 psi	2 in/min. ASTM D638
Ineos K44-08-122 HDPE K44-08-122 is a natural high density polyethylene copolymer designed specifically for extrusion of potable water, industrial, and mining pipe. It is recognized by the Plastic Pipe Institute as havin..
Tensile Strength at Break	31.0 MPa	4500 psi	ISO 527
SABIC Innovative Plastics LNP STAT-LOY A3000 ABS LNP STAT-LOY* A3000 is a compound based on ABS resin. Added feature of this material is: Antistatic.
Tensile Strength at Break	31.0 MPa	4500 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-LOY K3000SZ Acetal Copoly LNP* STAT-LOY* K3000SZ is a compound based on Acetal Copolymer resin. Added feature of this material is: AntiSstatic.
Tensile Strength at Break	31.0 MPa	4500 psi	ISO 527-2
Tisan TISOPLEN® 30% Talc Filled Heat Stabilized Copolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois..
Tensile Strength at Break	31.0 MPa	4500 psi	ASTM D638
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman.
Tensile Strength at Break	31.0 MPa	4500 psi	ASTM D638
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman.
Tensile Strength at Break	31.0 MPa	4500 psi	at max load; ASTM D638
A. Schulman PP 1632-01 Polypropylene Random Copolymer DescriptionPolypropylene PP 1632-01 is a polypropylene random copolymer produced utilizing unique catalyst and processing technology. It was designed for injection molding and stretch blow molding ..
Tensile Strength at Break	31.0 MPa	4500 psi	ASTM D638
A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman.
Tensile Strength at Break	31.0 - 34.6 MPa	4500 - 5020 psi	ASTM D638M
DSM Somos® NeXT Stereolithography (SLA) Prototyping Polymer Somos® NeXT combines stiffness and impact resistance which brings it close the performance of injection molded thermoplastics. It produces finished parts with tight tolerances and detailed features..
Tensile Strength at Break	31.0 MPa	4500 psi	50mm/min; ISO 527-2
Denka CL-430 Transparent Resin Polymer (MABS) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a..
Tensile Strength at Break	31.0 MPa	4500 psi	50 mm/min; ISO 527
Chi Mei Polylac® PA-747 ABS High impact
Tensile Strength at Break	31.0 MPa	4500 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Dow DMDA-8904 NT 7 High Density Polyethylene Resin DOW DMDA-8904 NT 7 is produced using UNIPOL™ process technology. It is intended for use in injection molding applications such as pails, industrial parts and other shipping containers. Information..
Tensile Strength at Break	31.0 MPa @Temperature 23.0 °C	4500 psi @Temperature 73.4 °F	ISO 527 (1BA bar)
DuPont Performance Polymers Hytrel® HTR8241 TPC-ET (Unverified Data**) Hytrel® HTR8241 is a 65 nom.Shore D, non discoloring stabilizer, plasticiser free high performance resin for extrusion; high viscosity; outstanding mechanical properties up to 120°C and excellent ..
Tensile Strength at Break	31.0 - 48.0 MPa	4500 - 6960 psi	ASTM D638
Arkema Group KYNAR® 460 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Broad molecular weight distribution. High stability in harsh thermal, chemical and ultraviolet environments. High toughness a..
Tensile Strength at Break	31.0 - 48.0 MPa	4500 - 6960 psi	ASTM D638
Arkema Group KYNAR® 460 Red Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Broad molecular weight distribution, pigmented. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, ..
Tensile Strength at Break	31.0 MPa	4500 psi	ASTM D638
Plastics Group Polifil® T-20 20% Talc-Reinforced Polypropylene Polifil® T series compounds are homopolymer polypropylene resins reinforced with asbestos-free talc. They possess high flex modulus, high deflection temperature, good chemical resistance and colora..
Tensile Strength at Break	31.0 MPa	4500 psi	ISO 527-2
Tisan TISOPLEN® 20% Talc Filled Heat Stabilized Homopolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois..
Tensile Strength at Break	31.0 MPa	4500 psi	ASTM D638
Petromont 7001 Medium Density Polyethylene Resin Petromont HDPE 7001 is a medium-density polyethylene hexene modified resin with an excellent balance of chemical resistance and durability. It is designed to be readily processed by flat die extrusi..
Tensile Strength at Break	31.0 MPa	4500 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-KON QD000I PA 6/10 LNP* STAT-KON* QD000I is a compound based on Nylon 6/10 resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.