A. Schulman FORMION™ FI 394 Ionomer
| Category | Polymer , Thermoplastic , Ionomer |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman FORMION™ FI 394 Ionomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ISO 1183/1 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 63 | 63 | Instantaneous; ISO 868 |
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | at max load; ISO 527 |
| Elongation at Break | 135 % | 135 % | ISO 527 |
| Flexural Modulus | 1.31 GPa | 190 ksi | Tangent; ISO 178 |
| Izod Impact, Notched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C @Thickness 3.20 mm |
165 °F @Thickness 0.126 in |
ISO 75 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering E50Q Ethylene Propylene Rubber
- Nilit FRIANYL B63 KV15 Nylon 6 for injection molding, 15% glass ball reinforced
- Plastcom PLASTALEN® PH 52 T 20 Polypropylene reinforced with mineral filler
- Lehmann & Voss LUVOCOM® 1301-8457 PPS, linear, with carbon fiber, lubricant modified
- Stir SpA B 3001 S AT (PVC)
- ChevronTexaco Compound L Rust Proof
- ExxonMobil Jayflex™ DIDP Plasticizer (European Grade)
- Alliance N-50 Neodymium Iron Boron Magnetic Material
- BASF Ultramid® B27 03 PA6
- Zhejiang Juner PC-A1-3 Top-Grade Flame Retardant UV-Resistant
Copyright © lookpolymers.com All Rights Reserved