RheTech Products M25UVP250-01 25% Mica Reinforced Polypropylene Copolymer, UV Stabilized, Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Mica Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products M25UVP250-01 25% Mica Reinforced Polypropylene Copolymer, UV Stabilized, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: BracketsCowl screensRigid exterior componentsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 25 % | 25 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 72 | 72 | ASTM D2240 |
| Tensile Strength at Break | 24.1 MPa | 3500 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 2.41 GPa | 350 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Temperature 23.0 °C |
0.900 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.565 J | 0.417 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 °C | 145 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Middle Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Front Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Nozzle Temperature | 216 - 227 °C | 420 - 440 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH TS15010 Polypropylene Homopolymer, Mineral Reinforced
- Parker Chomerics CHO-FOIL CCK Shielding Tape
- BP Amoco Amoco® 7942 Polypropylene Homopolymer (discontinued **)
- Indium Corp. Indalloy 148 Pure Bismuth
- Borealis Visico™ LE4421/LE4432 Scorch Retardant, Moisture-Crosslinking Polyethylene Compound for Low Voltage Installation
- ExxonMobil 46 Mobil EAL Envirosyn H Series
- A. Schulman POLYBATCH™ ABPP-05 Antiblock Concentrate
- Akzo Nobel Expancel® 051 WU 40 Wet unexpanded microspheres
- Axiall 7555 Rigid PVC, Extrusion, Natural
Copyright © lookpolymers.com All Rights Reserved