RheTech Products FT7013-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural
| Category | Polymer , Thermoplastic , Polyolefin |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products FT7013-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Scuff platesLift gate coversI/P componentsClose-out panelsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 28 % | 28 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 61 | 61 | ASTM D2240 |
| Tensile Strength at Break | 17.2 MPa | 2500 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.59 GPa | 230 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm @Temperature 23.0 °C |
4.00 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 18.0 J | 13.3 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.7 °C | 206 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.3 °C | 128 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Middle Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Front Barrel Temperature | 216 - 243 °C | 420 - 470 °F | |
| Nozzle Temperature | 221 - 232 °C | 430 - 450 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Multibase SILASTIC® C7-4565 CADOX BSD Dow-Corning Biomedical Grade ETR Elastomer
- Momentive Performance Materials Addisilâ„¢ 1080 E Industrial Extrusion Heat Cured Rubber
- Momentive Performance Materials RTV560 Red Extreme High Temperature Potting/Encapsulating Compound
- Lubrizol Advanced Materials Pearlstick® 45-90/03 Polycaprolactone based TPU
- Polyram RamSter PF300G8 PBT, 40% Glass Fiber
- Zeon Chemicals Nipol® 1042 Nitrile Elastomer
- Carpenter S7 Alloy Tool Steel (AISI S7)
- DSM Akulon® K224-PG3 Impact Modified Nylon 6-15% Glass Reinforced (European Grade) (Cond)
- Johnson Matthey Matti-phos 5 Alloy for Fluxless Brazing of Copper
Copyright © lookpolymers.com All Rights Reserved