- Polymer Property : Melt Flow = 12 g/10 min
Polymer Property : Melt Flow = 12 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 12 g/10 min @Load 0.325 kg, Temperature 270 °C |
12 g/10 min @Load 0.716 lb, Temperature 518 °F |
|
| Plastcom SLOVALEN PH 63 T 20 PP, 20% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 20% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc conte nt. Decreased sh.. |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| RheTech Products G13P100-589UV 13% Glass Fiber Reinforced Polypropylene, UV Stabilized, (YR169L) Mild Beige Applications: Interior trimAir ducts - distributionFuel filler pocketInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Melt Flow | 12 g/10 min @Load 6.60 kg, Temperature 400 °C |
12 g/10 min @Load 14.6 lb, Temperature 752 °F |
ASTM D1238 |
| SABIC Innovative Plastics EXTEM UH1016 TPI Blend (Europe-Africa-Middle East) High heat amorphous TPI Blend, Chemical Resistant, High Flow |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| PolyMirae Moplen HP601N Injection Molding Grade Polypropylene Moplen HP601N is the polypropylene homopolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen HP601N is a homopolymer typically used by customers in Glass Mat Sh.. |
|||
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Plaskolite West Optix® CA-927 G HF Clear Impact Modified Acrylic Resin Impact modified acrylic resin, injection molding gradeApplications: A high flow, impact-modified acrylic resin designed for medical or food uses. This resin offers impact strengths up to seven time.. |
|||
| Melt Flow | <= 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
<= 12 g/10 min @Load 2.65 lb, Temperature 572 °F |
|
| Lehmann & Voss LUVOCOM® 50/GF/10/TF/18/SI/2/GY5 Polycarbonate, with glass fiber, PTFE, lubricant modified Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Ineos N12N-00 Polypropylene Impact Copolymer Grade N12N-00 is a nucleated polypropylene impact copolymer with an excellent balance of stiffness and impact resistance for injection molding applications and compounding products used in Lawn and .. |
|||
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 230 °C |
12 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Inno-Comp INNOPOL® CS 1-5120 BLH 20% Talc-Filled Polypropylene Homopolymer INNOPOL® CS 1-5120 BLH is a 20% talc-filled polypropylene homopolymer compound /PP-H TD20 (ISO 1043)/.INNOPOL® CS 1-5120 BLH is recommended especially for producing products, where high stiffn.. |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Inno-Comp INNOPOL® CS 2-3120 20% Talc Filled Polypropylene Block-Copolymer INNOPOL® CS 2-3120 is a 20% talc filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-3120 is developed for producing.. |
|||
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| MRC Polymers NAXELL™ PC429MHI Polycarbonate, Impact Modified • Medium MFR• Good property retention, heat and dimensional stability• Available in natural and custom colors• Can be UV Stabilized• Internal and external lubricants ca.. |
|||
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 260 °C |
12 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Styron Pulse® 979 PC/ABS PULSE™ 979 is a high performance, 10% glass filled PC/ABS resin.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010. |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| SCG Chemicals EL-Proâ„¢ P702J Polypropylene Injection Molding Key Characteristics:High clarityHigh stiffnessGood processabilityMicrowavable for cooking applicationsOdorlessSafe for food contactRecommended Applications:General purpose injection parts that requi.. |
|||
| Melt Flow | 12 g/10 min @Load 8.70 kg, Temperature 190 °C |
12 g/10 min @Load 19.2 lb, Temperature 374 °F |
ASTM D1238 |
| Lubrizol Estane® X-590A-31 Thermoplastic Polyurethane Type: Estane® X-590A-31 is a Shore 91A, polyester grade without lubricant thermoplastic polyurethane (TPU). USP Class VI Certified.Uses: Extrusion, Film Blowing.Information Provided by The Lubrizo.. |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Borealis Bormed™ RE806CF Polypropylene Random Copolymer Bormed™ RE806CF is a random copolymer. The material is specially formulated for medical applications. Applications: Bormed™ RE806CF is recommended for medical packaging. Bormed™ RE806CF contai.. |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 235 °C |
12 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
| UBE UBESTA® 3020IX1 Rigid Automotive Grade Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: conductive, impact modifiedInformation provided by UBE. |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Red 5170 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 5170 is a red color concentrate based in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 5170 contains .. |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Blue 4012 Concentrate Based in Polyethylene DescriptionPOLYBATCH® 4012 is a blur color concentrate based in polyethylene. This concentrate was designed to provide opacity and color in polyolefin film and molding applications. POLYBATCH® 4.. |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Red 5170 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 5170 is a red color concentrate based in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 5170 contains .. |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Red 5170 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 5170 is a red color concentrate based in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 5170 contains .. |
|||
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Tipco Tipcolene® TPE 1000 - Impact Modified Polypropylene Copolymer Compound with High Stiffness High Impact PP CopolymerApplications: Automotive BumpersProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polyram RamOfin PPC501 Polypropylene, Flame Retardant Flame retardant polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Green 3315 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 3315 is a green color concentrate based in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 3315 is typi.. |
|||
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| A. Schulman POLYFLAM™ RPP 1058 General Purpose Homopolymer Polypropylene (30% Fiberglass) DescriptionPolyflam® RPP 1058 is a general purpose homopolymer polypropylene flame retardant with a UL-V2 flammability rating and 105°C temperature index at 0.030 in.Information provided by A. Sch.. |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| DuPont Performance Polymers Delrin® 500T BK602 Acetal (POM)
(Unverified Data**) Toughened Medium Viscosity Acetal Homopolymer Delrin 500T BK602 is a toughened medium viscosity acetal homopolymer resin with impact resistance similar to Delrin 100. It can be used in parts requiri.. |
|||
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Aclo Accutech Polypropylene Copolymer CP0436W30L1 Wollastonite Reinforced |
|||
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Aclo Accutech Polypropylene Homopolymer HP0336T30L1 Talc Reinforced |
|||
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Aclo Accutech Polypropylene Homopolymer HP0336W30L1 Wollastonite Reinforced |
|||
| Melt Flow | 12 g/10 min | 12 g/10 min | ISO 1133 D |
| Asahi Kasei Tenac® LT804 Homopolymer Acetal Resin Excellent friction and wear on metals.Information provided by Asahi Kasei Corporation. |
|||
| Melt Flow | 12 g/10 min @Load 10.0 kg, Temperature 220 °C |
12 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| LG Chemical LI912 ASA Description: Good Weatherability, General PurposeApplication: Mail Box, Sprinkler, Sash Joiner, Toy, Satellite Antenna CoverCAS: 26299-47-8Information provided by LG Chemical |
|||
| Melt Flow | 12 g/10 min @Load 2.16 kg |
12 g/10 min @Load 4.76 lb |
|
| Multibase Multibatch® MP 52658 BOPP Pearlised Film 70% CaCO3 FilledInformation provided by Multibase |
|||