PolyOne Nymax™ GF 1800 43 Black 22 Polyamide 612 (Nylon 612)
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Nymax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Nymax™ GF 1800 43 Black 22 Polyamide 612 (Nylon 612).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Property data for molded test bars: Dry as MoldedInformation provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Thickness 3.18 mm |
0.20 % @Thickness 0.125 in |
@ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 167 MPa | 24200 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
| Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
2.25 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 215 °C | 419 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C @Thickness 3.18 mm |
410 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 3.18 mm |
392 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black | |
| Filler / Reinforcement | Glass Fiber Reinforcement | |
| Unspecified FillerReinfor., 43% Filler by Weight | ||
| Forms | Pellets | |
| Generic Material | Nylon 612 | |
| Generic Name | Polyamide 612 (Nylon 612) | |
| Regional Availability | North America | |
| South America |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ MD 4245-1000 Polypropylene Copolymer (PP Copolymer)
- Nye Lubricants UniFlor 8521R (841RP-1) (UF) Synthetic Oil
- Precision Polymer Engineering S50N Silicone Rubber
- Lord Adhesives Fusor® 310 A/B Epoxy Adhesive
- Silberline Stamford "O" Standard Series
- Unifrax IsoMat® AV5 Substrate Support Mat
- Trelleborg Emerson & Cuming EP652 Patch Paste
- Loctite® 3492 Acrylic Light Cure Adhesive
- Hexcel® HexWeb® CRF-3/8-ACG-.002-2.3 Chromate free ACG® Honeycomb
- Solvay RHODAFAC® RA-600 E Surfactant
Copyright © lookpolymers.com All Rights Reserved