RheTech Products FT4700-01A Thermoplastic Polyolefin, Non-UV Stabilized, Black
| Category | Polymer , Thermoplastic , Polyolefin |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products FT4700-01A Thermoplastic Polyolefin, Non-UV Stabilized, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: CladdingsBodyside moldingsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.990 g/cc | 0.990 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 13 % | 13 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.17 GPa | 170 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 3.20 J/cm @Temperature 23.0 °C |
6.00 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 36.2 J | 26.7 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 215 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.1 °C | 124 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 - 221 °C | 380 - 430 °F | |
| Middle Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Front Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Nozzle Temperature | 210 - 221 °C | 410 - 430 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Nye Lubricants 920 (HSC) Synthetic Oil
- Michelman® Coating X300™ Plus Water based, moisture and water resistant coating
- SABIC Innovative Plastics ULTEM SF2350 PEI Blend (Asia Pacific)
- SABIC Innovative Plastics Xylex X7200 PC+POLYESTER (Asia Pacific)
- SABIC Innovative Plastics NORYL PX1391 PPE+PS (Asia Pacific)
- DuPont Teijin Films Teijin® Tetoron® HSL Polyester Film, 740 Gauge
- Covestro Bayblend® KU 2-1466 Polycarbonate/ABS Blend
- 3M 31U26C/UV Protective UV Tape
- Ametek AM 388™ Alloy (UNS C72650) TM06
- Hexcel® HexPly® 920KX-285-52% 125°C Curing Epoxy Matrix
Copyright © lookpolymers.com All Rights Reserved